An automotive battery pack for use in electric vehicles consists of a large number of individual battery cells that are structurally held and electrically connected. Making the required electrical and structural joints represents several challenges, including, joining of multiple and thin highly conductive/reflective materials of varying thicknesses, potential damage (thermal, mechanical, or vibrational) during joining, a high joint durability requirement, and so on. This paper reviews the applicability of major and emerging joining techniques to support the wide range of joining requirements that exist during battery pack manufacturing. It identifies the advantages, disadvantages, limitations, and concerns of the joining technologies. The maturity and application potential of current joining technologies are mapped with respect to manufacturing readiness levels (MRLs). Further, a Pugh matrix is used to evaluate suitable joining candidates for cylindrical, pouch, and prismatic cells by addressing the aforementioned challenges. Combining Pugh matrix scores, MRLs, and application domains, this paper identifies the potential direction of automotive battery pack joining.

This article presents the surface modification of aluminum workpiece by electric discharge coating (EDC) process using TiC/Cu green compact tool-electrode. Powder metallurgy (P/M) tool-electrodes were used to create hard layer(s) on the workpiece surface by a material transfer from this tool-electrode (produced with powder metallurgy) to the workpiece surface it was possible to create hard layer(s) there with high tribological properties and integrity. The present study has been carried out to investigate the effect of input parameters (peak current, pulse-on time, composition and compaction pressure of the tool-electrode) on process performance parameters (roughness and micro-hardness of workpiece surface and coating layer thickness). Regression models have been developed to define a mathematical correlation between input and process performance parameters. Analysis of variance has been conducted at the 95% confidence level, to test the significance of these models. The results of the experiments indicate that the regression models are highly significant. Confirmation experiments were conducted to validate the developed model. By the realization of “confirmation experiments,” it became evident that the developed regression models were correct and acceptable. Moreover, EDX analysis of worksample obtained of the workpiece surface has been carried out to confirm the process of material transferring mentioned above.

Lithium-ion-based secondary battery packs are emerging as an alternative power source and are being increasingly used in electric vehicles, hybrid or plug-in hybrid electric vehicles. Typically, a standard automotive battery pack consists of hundreds, even thousands, of individual cells which are connected in series and/or parallel to deliver the required power and capacity. There is an increasing need for manufacturing of battery packs to meet the demand reflecting the uptake of these vehicles. This triggers the need for suitable joining methods which will provide mechanical strength on a par with electrical and thermal characteristics. This work focuses on characterisation of shear strength of battery tab-to-tab joints for both similar and dissimilar materials by using combinations of aluminium (Al) and nickel-coated copper (Cu[Ni]) tabs. The joining techniques with application for battery tab interconnects are ultrasonic metal welding, resistance spot welding and pulsed TIG spot welding. Lap shear and T-peel tests are performed to evaluate the joint strength. In general, lap shear strength is four to seven times higher than the T-peel strength obtained from all three joining methods. In addition, an indicator is developed in this paper based on lap shear-to-T-peel strength reduction ratio which provides additional information on joint strength characteristics, and subsequently, it can be used as a threshold by quality engineers for an indication on selection of joining methods having an acceptable strength reduction ratio.

Recent uptake in the use of lithium-ion battery packs within electric vehicles has drawn significant attention to the selection of busbar material and corresponding thickness, which are usually based on mechanical, electrical and thermal characteristics of the welded joints, material availability and cost. To determine joint behaviour corresponding to critical-to-quality criteria, this study uses one of the widely used joining technologies, ultrasonic metal welding (UMW), to produce tab-to-busbar joints using copper and aluminium busbars of varying thicknesses. Joints for electrical and thermal characterisation were selected based on the satisfactory mechanical strength determined from the T-peel tests. Electrical contact resistance and corresponding temperature rise at the joints were compared for different tab-to-busbar joints by passing current through the joints. The average resistance or temperature increase from the 0.3 mm Al tab was 0.6 times higher than the 0.3 mm Cu[Ni] tab, irrespective of busbar selection.

This paper investigates the effects of process parameters on the joint strength and process robustness when multi-layered joints of dissimilar metals are produced by ultrasonic metal welding (UMW). Three layers of 0.3-mm aluminium sheet are welded with a single 1.0-mm copper sheet which is representative of electric vehicle battery interconnects. A process robustness study in which welding pressure, amplitude of vibration and welding time are varied to produce satisfactory welds is reported. The weld quality is evaluated by performing lap shear and T-peel tests where maximum loads are considered as the quality indicator. Response surfaces are developed to identify the relationship and sensitivity between the input process parameters and output quality indicators. A feasible weldability zone is defined for the first time by identifying the under-weld, good-weld and over-weld conditions based on load-displacement curves and corresponding failure modes. Relying on the weldability zone and response surfaces, multi-objective optimisation is performed to obtain maximum lap shear and T-peel strength which resulted in Pareto frontier or trade-off curve between both objectives. An optimal joint is selected from the Pareto front which is verified and validated by performing confirmation experiments, and further, used for T-peel strength analysis of different interfaces of the multi-layered joint. To conclude, this paper determines both the optimal weld parameters and the robust operating range.