The gear transmission system is a safety-critical component in rail transit, typically designed for a service life exceeding 20 years. Failure analysis of such systems remains a key focus for railway engineers. This study systematically investigates four representative cases of premature gear failure in high-speed trains using a standardized analytical procedure that includes visual inspection, chemical analysis, metallographic examination, scanning electron microscopy, and hardness testing. The results identify four primary root causes: subsurface slag inclusions in raw materials, inadequate heat treatment leading to a non-martensitic layer (∼60 μm) at the tooth root, grinding-induced temper burns (crescent-shaped "black spots") accompanied by a hardness drop of ∼100–150 HV, and insufficient lubrication. The interdependencies between these factors and failure mechanisms, e.g., fatigue cracking, spalling, and thermal scuffing, are analyzed. This work provides an evidence-based framework for improving gear reliability and proposes targeted countermeasures, such as ultrasonic inclusion screening and real-time grinding temperature control, to extend operational lifespans.

This study investigates premature fatigue failures in three EA1N steel axles from permanent magnet direct-drive locomotives during wheel-seat bending tests. Complete fracture occurred in one axle at 3 million cycles, and in the other two axles, cracks appeared and were observed through magnetic particle detection at 3.5 million and 1.6 million cycles, respectively. A comprehensive failure analysis was conducted through metallurgical examination, fractography, mechanical testing, residual stress measurement, and finite element analysis. The fractographic results revealed fractures consistently initiated at the wheel-seat to axle-body transition arc, exhibiting characteristic ratchet marks and beach patterns. The premature fracture mechanism was identified as a high-stress fatigue fracture. The residual stress measurements showed detrimental tensile stresses at the surface. Coupled with the operating stress, the stress on the axle exceeds fatigue strength, which accelerates the initiation and propagation of fatigue cracks. Based on these observations, the failure mechanism was identified, and preventive methods were proposed to reduce the risk of recurrence of the in-service axles.