Titanium dental implants are commonly used due to their biocompatibility and biochemical properties; blasted acid-etched Ti is used more frequently than smooth Ti surfaces. In this study, physico-chemical characterisation revealed important differences in roughness, chemical composition and hydrophilicity, but no differences were found in cellular in vitro studies (proliferation and mineralization). However, the deposition of proteins onto the implant surface might affect in vivo osseointegration. To test that hypothesis, protein layers formed on discs of both surface type after incubation with human serum were analysed. Using mass spectrometry (LC/MS/MS), 218 proteins were identified, 30 of which were associated with bone metabolism. Interestingly, Apo E, antithrombin and protein C adsorbed mostly onto blasted and acid-etched Ti, whereas the proteins of the complement system (C3) were found predominantly on smooth Ti surfaces. These results suggest that physico-chemical characteristics could be responsible for the differences observed in the adsorbed protein layer.

The interactions of implanted biomaterials with the host organism determine the success or failure of an implantation. Normally, their biocompatibility is assessed using in vitro tests. Unfortunately, in vitro and in vivo results are not always concordant; new, effective methods of biomaterial characterisation are urgently needed to predict the in vivo outcome. As the first layer of proteins adsorbed onto the biomaterial surfaces might condition the host response, mass spectrometry analysis was performed to characterise these proteins. Four distinct hybrid sol-gel biomaterials were tested. The in vitro results were similar for all the materials examined here. However, in vivo, the materials behaved differently. Six of the 171 adsorbed proteins were significantly more abundant on the materials with weak biocompatibility; these proteins are associated with the complement pathway. Thus, protein analysis might be a suitable tool to predict the in vivo outcomes of implantations using newly formulated biomaterials.