The Lovozero Alkaline Massif intruded through the Archaean granite-gneiss and Devonian volcaniclastic rocks about 360 million years ago, and formed a large (20 × 30 km) laccolith-type body, rhythmically layered in its lower part (the Layered Complex) and indistinctly layered and enriched in eudialyte-group minerals in its upper part (the Eudialyte Complex). The Eudialyte Complex is composed of two groups of rocks. Among the hypersolvus meso-melanocratic alkaline rocks (mainly malignite, as well as shonkinite, melteigite, and ijolite enriched with the eudialyte-group minerals, EGM), there are lenses of subsolvus leucocratic rocks (foyaite, fine-grained nepheline syenite, urtite with phosphorus mineralization, and primary lovozerite-group minerals). Leucocratic rocks were formed in the process of the fractional crystallization of melanocratic melt enriched in Fe, high field strength elements (HFSE), and halogens. The fractionation of the melanocratic melt proceeded in the direction of an enrichment in nepheline and a decrease in the aegirine content. A similar fractionation path occurs in the Na₂O-Al₂O₃-Fe₂O₃-SiO₂ system, where the melt of the “ijolite” type (approximately 50% of aegirine) evolves towards “phonolitic eutectic” (approximately 10% of aegirine). The temperature of the crystallization of subsolvus leucocratic rocks was about 550 °C. Hypersolvus meso-melanocratic rocks were formed at temperatures of 700–350 °C, with a gradual transition from an almost anhydrous HFSE-Fe-Cl/F-rich alkaline melt to a Na(Cl, F)-rich water solution. Devonian volcaniclastic rocks underwent metasomatic treatment of varying intensity and survived in the Eudialyte Complex, some remaining unchanged and some turning into nepheline syenites. In these rocks, there are signs of a gradual increase in the intensity of alkaline metasomatism, including a wide variety of zirconium phases. The relatively high fugacity of fluorine favored an early formation of zircon in apo-basalt metasomatites. The ensuing crystallization of aegirine in the metasomatites led to an increase in alkali content relative to silicon and parakeldyshite formation. After that, EGM was formed, under the influence of Ca-rich solutions produced by basalt fenitization.

The Kovdor phoscorite-carbonatite ore-pipe rocks form a natural series, where apatite and magnetite first gradually increase due to the presence of earlier crystallizing forsterite in the pipe marginal zone and then decrease as a result of carbonate development in the axial zone. In all lithologies, magnetite grains contain (oxy)exsolution inclusions of comparatively earlier ilmenite group minerals and/or later spinel, and their relationship reflects the concentric zonation of the pipe. The temperature and oxygen fugacity of titanomagnetite oxy-exsolution decreases in the natural rock sequence from about 500 °C to about 300 °C and from NNO + 1 to NNO − 3 (NNO is Ni-NiO oxygen fugacity buffer), with a secondary positive maximum for vein calcite carbonatite. Exsolution spinel forms spherical grains, octahedral crystals, six-beam and eight-beam skeletal crystals co-oriented with host magnetite. The ilmenite group minerals occur as lamellae oriented along {111} and {100} planes of oxy-exsolved magnetite. The kinetics of inclusion growth depends mainly on the diffusivity of cations in magnetite: their comparatively low diffusivities in phoscorite and carbonatites of the ore-pipe internal part cause size-independent growth of exsolution inclusions; while higher diffusivities of cations in surrounding rocks, marginal forsterite-rich phoscorite and vein calcite carbonatite result in size-dependent growth of inclusions.

The use of mining and metallurgical waste for the production of building supplies reduces the burden on the environment and serves the sustainable development of the region’s industry at the same time. Russia has substantiated the possibility of producing ceramic construction materials of compression molding from a unique mixture of substances based on waste slag of copper–nickel productions, tailings of enrichment of apatite–nepheline ores, and ferruginous quartzites of enterprises of the Murmansk region. The effect of forming pressure (20, 50, and 100 MPa) on the properties of ceramic materials was studied. It is shown that an increase in molding pressure leads to an increase in the physical and mechanical properties of ceramic materials and to a decrease in fire shrinkage and water absorption. The use of a forming pressure of 100 MPa and a firing temperature of 1050 °C makes it possible to obtain a wall clinker brick; at a firing temperature of 1100 °C and a forming pressure of 20–100 MPa, a road clinker brick can be produced. Ceramic samples with frost resistance of more than 200 cycles were received.

The pyrochlore supergroup minerals (PSM) are typical secondary phases that replace (with zirconolite–laachite) earlier Sc-Nb-rich baddeleyite under the influence of F-bearing hydrothermal solutions, and form individual well-shaped crystals in surrounding carbonatites. Like primary Sc-Nb-rich baddeleyite, the PSM are concentrated in the axial carbonate-rich zone of the phoscorite-carbonatite complex, so their content, grain size and chemical diversity increase from the pipe margins to axis. There are 12 members of the PSM in the phoscorite-carbonatite complex. Fluorine- and oxygen-dominant phases are spread in host silicate rocks and marginal carbonate-poor phoscorite, while hydroxide-dominant PSM occur mainly in the axial carbonate-rich zone of the ore-pipe. Ti-rich PSM (up to oxycalciobetafite) occur in host silicate rocks and calcite carbonatite veins, and Ta-rich phases (up to microlites) are spread in intermediate and axial magnetite-rich phoscorite. In marginal (apatite)-forsterite phoscorite, there are only Ca-dominant PSM, and the rest of the rocks include Ca-, Na- and vacancy-dominant phases. The crystal structures of oxycalciopyrochlore and hydroxynatropyrochlore were refined in the $Fd\overline{3}m$ space group with R₁ values of 0.032 and 0.054 respectively. The total difference in scattering parameters of B sites are in agreement with substitution scheme ^BTi⁴⁺ + ^YOH^‒ = ^BNb⁵⁺ + ^YO^2‒. The perspective process flow diagram for rare-metal “anomalous ore” processing includes sulfur-acidic cleaning of baddeleyite concentrate from PSM and zirconolite–laachite impurities followed by deep metal recovery from baddeleyite concentrate and Nb-Ta-Zr-U-Th-rich sulfatic product from its cleaning.

The Kovdor alkaline-ultrabasic massif (NW Russia) is formed by three consequent intrusions: peridotite, foidolite–melilitolite and phoscorite–carbonatite. Forsterite is the earliest mineral of both peridotite and phoscorite–carbonatite, and its crystallization governed evolution of magmatic systems. Crystallization of forsterite from Ca-Fe-rich peridotite melt produced Si-Al-Na-K-rich residual melt-I corresponding to foidolite–melilitolite. In turn, consolidation of foidolite and melilitolite resulted in Fe-Ca-C-P-F-rich residual melt-II that emplaced in silicate rocks as a phoscorite–carbonatite pipe. Crystallization of phoscorite began from forsterite, which launched destruction of silicate-carbonate-ferri-phosphate subnetworks of melt-II, and further precipitation of apatite and magnetite from the pipe wall to its axis with formation of carbonatite melt-III in the pipe axial zone. This petrogenetic model is based on petrography, mineral chemistry, crystal size distribution and crystallochemistry of forsterite. Marginal forsterite-rich phoscorite consists of Fe²⁺-Mn-Ni-Ti-rich forsterite similar to olivine from peridotite, intermediate low-carbonate magnetite-rich phoscorite includes Mg-Fe³⁺-rich forsterite, and axial carbonate-rich phoscorite and carbonatites contain Fe²⁺-Mn-rich forsterite. Incorporation of trivalent iron in the octahedral M1 and M2 sites reduced volume of these polyhedra; while volume of tetrahedral set has not changed. Thus, trivalent iron incorporates into forsterite by schema (3Fe²⁺)_oct → (2Fe³⁺ + □)_oct that reflects redox conditions of the rock formation resulting in good agreement between compositions of apatite, magnetite, calcite and forsterite.