Composite stretchable conducting wires: Think how useful a stretchable electronic “skin” could be. For example you could place it over an aircraft fuselage or a body to create a network of sensors, processors, energy stores, or artificial muscles. But it is difficult to make electronic interconnects and strain sensors that can stretch over such surfaces. Liu et al. created superelastic conducting fibers by depositing carbon nanotube sheets onto a prestretched rubber core (see the Perspective by Ghosh). The nanotubes buckled on relaxation of the core, but continued to coat it fully and could stretch enormously, with relatively little change in resistance. Science , this issue p. 400 ; see also p. 382

Graphene and two-dimensional transition metal carbides and/or nitrides (MXenes) are important materials for making flexible energy storage devices because of their electrical and mechanical properties. It remains a challenge to assemble nanoplatelets of these materials at room temperature into in-plane isotropic, free-standing sheets. Using nanoconfined water-induced basal-plane alignment and covalent and π-π interplatelet bridging, we fabricated Ti ₃ C ₂ T _x MXene-bridged graphene sheets at room temperature with isotropic in-plane tensile strength of 1.87 gigapascals and moduli of 98.7 gigapascals. The in-plane room temperature electrical conductivity reached 1423 siemens per centimeter, and volumetric specific capacity reached 828 coulombs per cubic centimeter. This nanoconfined water-induced alignment likely provides an important approach for making other aligned macroscopic assemblies of two-dimensional nanoplatelets.

The effects of processing conditions and apparent nanotube length on properties are investigated for carbon nanotube yarns obtained by solid-state drawing of an aerogel from a forest of multi-walled carbon nanotubes. Investigation of twist, false twist, liquid densification and combination methods for converting the drawn aerogel into dense yarn show that permanent twist is not needed for obtaining useful mechanical properties when nanotube lengths are long compared with nanotube diameters. Average mechanical strengths of 800 MPa were obtained for polymer-free twist-spun multi-walled carbon nanotube (MWNT) yarns and average mechanical strengths of 1040 MPa were obtained for MWNT yarns infiltrated with 10 wt% polystyrene solution. Strategies for increasing the mechanical properties are suggested based on analysis of intra-wall, intra-bundle and inter-bundle stress transfer.

Actuation is normally dramatically enhanced by introducing so much yarn fiber twist that the fiber becomes fully coiled. In contrast, we found that usefully high muscle strokes and contractile work capacities can be obtained for non-twisted MXene (Ti ₃ C ₂ T _x ) fibers comprising MXene nanosheets that are stacked in the fiber direction. The MXene fiber artificial muscles are called MFAMs. We obtained MFAMs that have high modulus in both the radial and axial directions by spinning a solution containing MXene nanosheets dispersed in an aqueous cellulose solution. We observed a highly reversible muscle contraction of 21.0% for a temperature increase from 25° to 125°C. The tensile actuation of MFAMs mainly results from reversible hydrogen bond orientation change during heating, which decreases intra-sheet spacing. The MFAMs exhibited fast, stable actuation to multiple temperature-generating stimuli, which increases their applications in smart textiles, robotic arms, and robotic grippers.

Methods for making high-spring-index polymer fiber or yarn muscles have required expensive fabrication by wrapping around a mandrel, which limits their practical applications. We demonstrate an inexpensive mandrel-free method for making polymer muscles that can have a spring index of >50 and a contractile tensile stroke exceeding 97%. This method enables the spring index to be varied along a muscle’s length by varying the plying twist, resulting in muscles that transition between homochiral and heterochiral when either heated or cooled. We demonstrate use of these polymer muscles for robots and environmentally driven comfort-adjusting jackets. This mandrel-free method was used to make high-spring-index carbon nanotube yarns for mechanical energy harvesters, self-powered strain sensors, and solvent-driven and electrochemically driven artificial muscles.