Multi–principal element alloys (MPEAs) exhibit outstanding mechanical properties because the core effect of severe atomic lattice distortion is distinctly different from that of traditional alloys. However, at the mesoscopic scale the underlying physics for the abundant dislocation activities responsible for strength-ductility synergy has not been uncovered. While the Eshelby mean-field approaches become insufficient to tackle yielding and plasticity in severely distorted crystalline solids, here we develop a three-dimensional discrete dislocation dynamics simulation approach by taking into account the experimentally measured lattice strain field from a model FeCoCrNiMn MPEA to explore the heterogeneous strain-induced strengthening mechanisms. Our results reveal that the heterogeneous lattice strain causes unusual dislocation behaviors (i.e., multiple kinks/jogs and bidirectional cross slips), resulting in the strengthening mechanisms that underpin the strength-ductility synergy. The outcome of our research sheds important insights into the design of strong yet ductile distorted crystalline solids, such as high-entropy alloys and high-entropy ceramics.

Twin boundary (TB) plays an important role on the plastic deformation of high entropy alloy (HEA). The strong effects of TB on the deformation response of HEA are revealed from atomic level based on the defect structure, shear strain and surface morphology, by comparing the nanoindentation behavior of nanotwinned FeNiCrCoCu HEA (nt-HEA) and single-crystal FeNiCrCoCu HEA (single-HEA). The plastic deformation of nt-HEA is mainly dominated by the dislocations slip confined by first twinning layer, the TB migration, the dislocation nucleation at TB and the stacking fault tetrahedron (SFT) formation, while the dislocation loop emission is the main plastic deformation feature of single-HEA. Compared to the case for single-HEA, the nanoindentation induces more dislocations in nt-HEA. The shear strain in nt-HEA mainly distributes in the first twinning layer, due to the obstacle effect of TB. The shear zone is larger in nt-HEA, and the distribution of shear strain on the nt-HEA surface is more symmetric. The nanoindentation generates fewer steps on the nt-HEA surface, and then brings about a relatively smooth surface for nt-HEA. These findings provide an insight into the TB effect on the nanoindentation response of FeNiCrCoCu HEA, and develop the application of nanotwinned HEA systems.

Materials with excellent high-temperature strength are now sought for applications in hypersonics, fusion reactors, and aerospace technologies. Conventional alloys and eutectic multiprincipal-element alloys (MPEAs) exhibit insufficient strengths at high temperatures due to low melting points and microstructural instabilities. Here, we report a strategy to achieve exceptional high-temperature microstructural stability and strength by introducing eutectic carbide in a refractory MPEA. The synergistic strengthening effects from the multiprincipal-element mixing and strong dislocation blocking at the interwoven metal-carbide interface make the eutectic MPEA not only have outstanding high-temperature strength (>2 GPa at 1473 K) but also alleviate the room-temperature brittleness through microcrack tip blunting by layered metallic phase. This strategy offers a paradigm for the design of the next-generation high-temperature materials to bypass the low–melting point limitation of eutectic alloys and diffusion-dominated softening in conventional superalloys.