The prevention of implant-associated infections has been increasing clinically in orthopedic surgery. Hydroxyapatite with antibacterial properties was synthesized using a microwave-assisted combustion method. High crystallinity at low temperature can be achieved using this method. The synthesized hydroxyapatite exhibited a superior clear zone for both Gram-positive and Gram-negative bacteria. Electron spin resonance (ESR) and X-ray photoelectron spectroscopy (XPS) were used for the radical investigation. The application of intelligent ink testing and an antioxidant assay using DPPH reduction were also used to confirm the existence of radicals. These techniques provided data confirming that radicals are responsible for the antibacterial properties. The synthesized antibacterial hydroxyapatite would be a good candidate for the prevention any infection with medical implants and injection materials causing failure in bone repair.

Colored ZBP glasses with multiple catalytic properties have been successfully synthesized using a one-step melt-quenching technique.

Pathological mandibular fracture after dental extraction usually occurs in dogs with moderate to severe periodontitis. A nanohydroxyapatite-based hydrogel (HAP hydrogel) was developed to diminish the limitations of hydroxyapatite for post-extraction socket preservation (PSP). However, the effect of the HAP hydrogel in dogs has still not been widely investigated. Moreover, there are few studies on PSP in dogs suffering from clinical periodontitis. The purpose of this study was to evaluate the effectiveness of the HAP hydrogel for PSP in dogs with periodontitis. In five dogs with periodontitis, the first molar (309 and 409) of each hemimandible was extracted. Consequently, all the ten sockets were filled with HAP-hydrogel. Intraoral radiography was performed on the day of operation and 2, 4, 8 and 12 weeks post operation. The Kruskal–Wallis test and paired t-test were adopted for alveolar bone regeneration analysis. The results demonstrated that the radiographic grading, bone height measurement, and bone regeneration analysis were positively significant at all follow-up times compared to the day of operation. Moreover, the scanning electron microscopy with energy-dispersive X-ray spectroscopy imaging after immersion showed a homogeneous distribution of apatite formation on the hydrogel surface. Our investigation suggested that the HAP hydrogel effectively enhances socket regeneration in dogs with periodontitis and can be applied as a bone substitute for PSP in veterinary dentistry.