During the production of single-crystal superalloy blades, a kind of channel-type defect, named “quasi-freckle”, was found on the casting surface, which is similar to typical freckles in macroscopic appearance but different in microstructure. In the as-cast microstructure of the quasi-freckle channels, the γ/γ’ eutectic is significantly accumulated and can be dissolved during the solution heat treatment. Since no disoriented grains were detected, the quasi-freckles have a basically identical crystal orientation with the matrix. The quasi-freckle channels actually appear as thermosolutal convection traces in the directional solidification process of single-crystal casting. Because the convection was not strong enough to break dendrite arms, the single-crystal consistency of the castings was not destroyed. However, with the deterioration of the solidification condition and the increase in solutal convection, quasi-freckles often develop into typical freckle defects.