Graphene stratiform membrane materials have been recently applied to heavy metal removal in aqueous systems via adsorption due to their high mechanical strength, chemical stability, and other properties. We applied reduced graphene oxide (rGO) alone as an adsorbent to remove heavy metal ions from wastewater. Self-supported rGO membrane was prepared using a green reduction method with sodium hydrosulfite. We used the Raman spectra to observe the structure of the rGO membrane. The morphology of the self-supported membrane was measured by a scanning electron microscope. The Cu²⁺ adsorption performance was measured in terms of pH, reaction time, metal ion concentration, and temperature. The maximum Cu²⁺ adsorption capacity of the rGO membrane was found to be 149.25 mg/g. The adsorption process followed a pseudo-second-order kinetic model, and adsorption isotherms were simulated by the Freundlich model.

Windmill Palm Fiber/Polyvinyl Alcohol Coated Nonwoven Mats with Sound Absorption Characteristics

In this work, windmill palm fiber (WPF), alkali-treated fiber (AF) without hemicellulose and bleached fiber (BF) without lignin were prepared and buried in soil for 30, 60 and 90 days. The surface morphology, chemical composition, crystallinity degree, mechanical properties, and residual mass rate of the samples, before and after biodegradation, were investigated. According to the results, soil burial degradation can remove the parenchyma cells and silica-bodies of WPF and deplete droplets containing the lignin of alkali-treated fiber after it has been buried for 30 days (AF30), and degradation of the single fiber cell wall of bleached fiber after it has been buried for 30 days (BF30). Buried in natural soil, lignin has a slower degradation rate than that of hemicellulose. WPF showed no significant differences in tensile strength after burial in soil for 90 days, because of the integrity fiber structure decreased the biodegradation. The most serious decrease, about 43%, in tensile strength occurred in AF after it had been buried for 90 days (BF90). This basic knowledge may be helpful for windmill palm fiber applications, especially for biodegradable composites.