In this study, we presented the synthesis of LaNi_0.3Co_0.7O_3−δ (LNCO) and SrCo_0.8Fe_0.2O_3−δ (SFCO) perovskites and their catalytic reactivity under CO gas flow. The synthesis method is based on the complexation method combining ethylenediaminetetraacetic acid (EDTA)-citrate. The as-prepared materials were characterized using X-ray diffraction/Rietveld refinement and electron microscopy. The diffractograms and Rietveld refinement showed that the EDTA-citrate method allows us to obtain monophasic powders with submicronic size. The structural analyses revealed different morphologies linked to the crystallinity of LNCO and SFCO, and to the mean crystallite size. The catalytic performances of LNCO and SFCO were studied in situ by Fourier Transform InfraRed spectrometer as a function of time and temperature. The catalytic process gave rise to total oxidation with carbon dioxide and water production. LNCO and SFCO exhibit the same profile for catalytic activity with a conversion rate of twice as high for LNCO. Below 150 °C, the kinetic conversion is slow, but beyond this temperature they reach rapidly the complete transformation at 250 °C and 275 °C for LNCO and SFCO, respectively.

RESUMO No presente trabalho foi realizada a estimativa das emissões dos gases de efeito estufa (CO2eq), monóxido de carbono (CO), óxido de nitrogênio (NOx), material particulado (MP), aldeído (RCHO) e hidrocarboneto não metano (NMHC) dos veículos licenciados nos cinco primeiro meses do ano de 2020 no Brasil. Os resultados foram comparados com as emissões veiculares da frota licenciada no mesmo período do ano de 2019 a fim de verificar o impacto da pandemia de COVID-19 nos referidos licenciamentos, nas emissões e, consequentemente, na qualidade do ar do país. Os resultados apontaram redução de 14% nas emissões dos gases de efeito estufa, com diminuição observada para todos os veículos, exceto para os caminhões semipesados, que tiveram incremento nas emissões de gases de efeito estufa de 12,8%. Os demais poluentes também reduziram, em 12,5% para o CO, em 29,6% para o NOx, em 24,1% para o MP, em 21,5% para o RCHO e em 16,3% para o NMHC. Por fim, quanto ao total de poluentes acumulados, entre todos os veículos analisados, os únicos que tiveram aumento nas emissões em relação a 2019, de 2,1%, foram as motocicletas com tecnologia flexfuel, que são abastecidas preferencialmente com etanol hidratado. Com isso, pôde-se concluir que a pandemia da COVID-19, por meio das medidas de restrição e isolamento social adotadas no país para frear a transmissão da doença, impactou positivamente a qualidade do ar no Brasil no período analisado.

In this study, nanostructured ferberites (FeWO₄) were synthesized via hydrothermal routes in an acidic medium. It was then investigated as an efficient photocatalyst for degrading organic dye molecules, with methylene blue (MB) as a model pollutant. The formation mechanism of ferberite revealed that the physical form of the precursor, FeSO₄·7H₂O, acts as a decisive factor in morphological evolution. Depending on whether it is in a solid or dilute solution form, two distinct nanostructures are produced: nanoplatelets and self-organized microspheres. Both structures are composed of stoichiometric FeWO₄ (Fe: 49%, W: 51%) in a single monoclinic phase (space group P2/c:1) with high purity and crystallinity. The p-type semiconductor behavior was confirmed using Mott–Schottky model and the optical analysis, resulting in small band gap energies (≈1.7 eV) favoring visible absorption light. Photocatalytic tests under simulated solar irradiation revealed rapid and efficient degradation in less than 10 min under near-industrial conditions (pH 5). This was achieved using only a ferberite catalyst and a low concentration of H₂O₂ (4 mM) without additives, dopants, or artificial light sources. Advanced studies based on photocurrent measurements, trapping and stability tests were carried out to identify the main reactive species involved in the photocatalytic process and better understanding of photodegradation mechanisms. These results demonstrate the potential of nanostructured FeWO₄ as a sustainable and effective photocatalyst for water purification applications.

RESUMO A indústria têxtil consome um volume significativo de água no processo de tingimento das fibras. As águas residuais geradas no processamento, além de turvas, devido à presença de corantes que não se fixam na fibra durante o processo de tingimento, são prejudiciais ao ambiente aquático e também aos seres humanos. Esse efluente deve passar por um processo de tratamento antes de ser lançado em corpos hídricos. O tratamento de águas contaminadas com o uso de bioadsorventes possui como vantagens o baixo custo de material e reciclagem de resíduo natural. Baseado no exposto, o objetivo deste trabalho foi avaliar a capacidade de adsorção do corante têxtil Azul Reativo BF-5G em casca de mandioca (Manihot Esculenta Crantz), resíduo proveniente da indústria de farinha de mandioca. A casca de mandioca foi lavada, seca e classificada. Os ensaios de adsorção, em banho finito, foram realizados em diferentes condições de pH, granulometria e temperatura. As capacidades máximas de adsorção, em 24 horas de contato, para as diferentes condições de pH, granulometria e temperatura, foram as seguintes: (qmáx=85,18 mg.g-1; pH=1; 30 °C; 16 mesh); (qmáx=52,30 mg.g-1; pH=0; 30 °C; 32 mesh); (qmáx=92,92 mg.g-1; pH=0; 30 °C; 48 mesh). O processo de adsorção foi espontâneo e exotérmico, o que leva a concluir que a casca de mandioca (Manihot Esculenta Crantz) é um potencial adsorvente para o corante Azul Reativo BF-5G, garantindo economia e praticidade no tratamento desse efluente.

A perovskita de cerato de bário foi sintetizada com base no método de complexação combinando EDTA-citrato e suas propriedades catalíticas testadas na reação de oxidação do monóxido de carbono em um reator de leito fixo variando a vazão de alimentação (50 e 100 mL.min^-1) e a temperatura (100 a 550 °C). A fase cristalina de interesse foi obtida com tamanho de cristalito de 133 nm, junto com uma pequena quantidade de BaCO₃ (3%). Quando sintetizado pelo método de complexação combinando EDTA-citrato, o cerato de bário apresenta um formato esférico irregular com aglomerados de diferentes tamanhos e com a presença de poros de diferentes tamanhos distribuídos aleatoriamente, sendo sua área superficial específica igual a 2,61 m².g^-1. Na vazão de 50 mL.min^-1 ocorreu maior conversão quando comparado com a de 100 mL.min^-1, sendo mais evidente entre 300 e 400 °C. Além disso, na vazão de 50 mL.min^-1 ocorreu conversão total de CO em CO₂ a 400 °C, enquanto que em 100 mL.min^-1 a conversão foi de aproximadamente 60%. Com o uso da perovskita como catalisador o processo de oxidação é completo a 400 °C, enquanto que na reação sem catalisador a conversão completa é alcançada somente a 550 °C. Apesar da sua pequena área superficial, o BaCeO₃ é altamente reativo na oxidação do monóxido de carbono.