The constantly evolving electrification also entails an increase in requirements for the effective and efficient distribution of electricity with the lowest possible power losses. Such needs can be met by highly effective electrical devices, and one of them is a transformer whose main component is a magnetic core. Currently, one of the soft magnetic materials used alternatively for the production of transformer cores are amorphous metal strips with competitive losses. However, to successfully use these materials, a key problem must be solved: limited mechanical stability. The presented article describes the development and application of a polyimide-based binder for efficient bonding of an amorphous metal ribbon. The layered binder was characterized using confocal microscopy, scanning electron microscopy and Raman spectroscopy, and its anticorrosion and mechanical properties were examined. As a final step, a prototype of a toroidal magnetic core bonded with the binder was manufactured and subjected to the evaluation of no-load loss and the analysis of the emitted noise. It was confirmed that the proposed polyimide binder tremendously improved the mechanical stability while reducing core losses and audible noise.

The ongoing electrification process also requires improvements in the efficiency of power transmission devices, such as transformers, the main part of which is the magnetic core. Despite great progress in the development of core material, losses and audible noise during their operation is still a critical issue to be solved. Currently, a magnetic material used to produce the transformer core is amorphous steel, which is gaining popularity. Compared to traditionally used grain-oriented silicon electrical steel, a significantly larger number of very thin amorphous ribbons is needed to produce the core, which is due to the fact that they are about an order of magnitude thinner, making mechanical stability a challenge. The presented article describes the preparation of a hybrid binder for amorphous steel based on the two types of silanes, tetraethyl orthosilicate and 1,2-bis(triethoxysilyl)ethane, for which their anticorrosive character and good dielectric properties were confirmed. Using the obtained binders, model toroidal cores were produced and their magnetic and acoustic properties were tested. The obtained results indicate that the applied silane-based hybrid binders improved important functional properties by reducing the magnetic no-load losses and audible noise.