Few-wall carbon nanotubes were synthesized by methane/acetylene decomposition over bimetallic Fe-Mo catalyst with MgO (1:8:40) support at the temperature of 900°C. No calcinations and reduction pretreatments were applied to the catalytic powder. The transmission electron microscopy investigation showed that the synthesized carbon nanotubes [CNTs] have high purity and narrow diameter distribution. Raman spectrum showed that the ratio of G to D band line intensities of I G/I D is approximately 10, and the peaks in the low frequency range were attributed to the radial breathing mode corresponding to the nanotubes of small diameters. Thermogravimetric analysis data indicated no amorphous carbon phases. Experiments conducted at higher gas pressures showed the increase of CNT yield up to 83%. Mössbauer spectroscopy, magnetization measurements, X-ray diffraction, high-resolution transmission electron microscopy, and electron diffraction were employed to evaluate the nature of catalyst particles.

Simultaneous mass production of high quality vertically oriented graphene nanostructures and doping them by using an inductively coupled plasma chemical vapor deposition (ICP CVD) is a technological problem because little is understood about their growth mechanism over enlarged surfaces. We introduce a new method that combines the ICP CVD with roll-to-roll technology to enable the in-situ preparation of vertically oriented graphene by using propane as a precursor gas and nitrogen or silicon as dopants. This new technology enables preparation of vertically oriented graphene with distinct morphology and composition on a moving copper foil substrate at a lower cost. The technological parameters such as deposition time (1–30 min), gas partial pressure, composition of the gas mixture (propane, argon, nitrogen or silane), heating treatment (1–60 min) and temperature (350–500 °C) were varied to reveal the nanostructure growth, the evolution of its morphology and heteroatom’s intercalation by nitrogen or silicon. Unique nanostructures were examined by FE-SEM microscopy, Raman spectroscopy and energy dispersive X-Ray scattering techniques. The undoped and nitrogen- or silicon-doped nanostructures can be prepared with the full area coverage of the copper substrate on industrially manufactured surface defects. Longer deposition time (30 min, 450 °C) causes carbon amorphization and an increased fraction of sp³-hybridized carbon, leading to enlargement of vertically oriented carbonaceous nanostructures and growth of pillars.

Femtosecond lasers (FSL) are playing an increasingly important role in materials research, characterization, and modification. Due to an extremely short pulse width, interactions of FSL irradiation with solid surfaces attract special interest, and a number of unusual phenomena resulted in the formation of new materials are expected. Here, we report on a new nanostructure observed after the interaction of FSL irradiation with arrays of vertically aligned carbon nanotubes (CNTs) intercalated with iron phase catalyst nanoparticles. It was revealed that the FSL laser ablation transforms the topmost layer of CNT array into iron phase nanospheres (40 to 680 nm in diameter) located at the tip of the CNT bundles of conical shape. Besides, the smaller nanospheres (10 to 30 nm in diameter) are found to be beaded at the sides of these bundles. Some of the larger nanospheres are encapsulated into carbon shells, which sometime are found to contain CNTs. The mechanism of creation of such nanostructures is proposed.

Erbium upconversion (UC) photoluminescence (PL) from sol-gel derived barium titanate (BaTiO₃:Er) xerogel structures fabricated on silicon, glass or fused silica substrates has been studied. Under continuous-wave excitation at 980 nm and nanosecond pulsed excitation at 980 and 1540 nm, the fabricated structures demonstrate room temperature PL with several bands at 410, 523, 546, 658, 800 and 830 nm, corresponding to the ²H_9/2 → ⁴I_15/2, ²H_11/2 → ⁴I_15/2, ⁴S_3/2 → ⁴I_15/2, ⁴F_9/2→ ⁴I_15/2 and ⁴I_9/2→ ⁴I_15/2 transitions of Er³⁺ ions. The intensity of erbium UC PL increases when an additional macroporous layer of strontium titanate is used beneath the BaTiO₃ xerogel layer. It is also enhanced in BaTiO₃ xerogel films codoped with erbium and ytterbium (BaTiO₃:(Er,Yb)). For the latter, a redistribution of the intensity of the PL bands is observed depending on the excitation conditions. A multilayer BaTiO₃:(Er,Yb)/SiO₂ microcavity structure was formed on a fused silica substrate with a cavity mode in the range of 650–680 nm corresponding to one of the UC PL bands of Er³⁺ ions. The obtained cavity structure annealed at 450 °C provides tuning of the cavity mode by 10 nm in the temperature range from 20 °C to 130 °C. Photonic application of BaTiO₃ xerogel structures doped with lanthanides is discussed.

Sol-gel technology has attracted attention in the fabrication of diverse luminescent materials and thin film structures, with forms that range from powders to microcavities. The optical properties of sol-gel-derived structures depend on the sol composition, deposition, and heat treatment conditions, as well as on the film thicknesses and other factors. Investigations on the upconversion luminescence of lanthanides in film structures and materials are also ongoing. In this study, we synthesized three different types of materials and film structures using the same sol, which corresponded to a Ba_0.76Er_0.04Yb_0.20TiO₃ xerogel, as follows: (a) the target form, which used the explosive compaction method for sol-gel-derived powder; (b) single-layer spin-on xerogel films annealed at 450 and 800 °C; and (c) microcavities with an undoped SiO₂/BaTiO₃ Bragg reflector surrounding a Ba_0.76Er_0.04Yb_0.20TiO₃ active layer. The BaTiO₃:(Er,Yb)/SiO₂ microcavity exhibited an enhancement of the upconversion luminescence when compared to the BaTiO₃:(Er,Yb) double-layer film fabricated directly on a crystalline silicon substrate. The reflection spectra of the BaTiO₃:(Er, Yb)/SiO₂ microcavity annealed at 800 °C demonstrated a deviation of the maxima of the reflection within 15% for temperature measurements ranging from 26 to 120 °C. From the analyses of the transmission and reflection spectra, the optical band gap for the indirect optical transition in the single layer of the BaTiO₃:(Er,Yb) spin-on film annealed at 450 °C was estimated to be 3.82 eV, while that for the film annealed at 800 °C was approximately 3.87 eV. The optical properties, upconversion luminescence, and potential applications of the BaTiO₃:(Er,Yb) sol-gel-derived materials and structures are discussed in this paper.