Al-Ni-Cu alloys are used in energy, automotive, and aerospace industries because of their excellent mechanical properties, corrosion resistance, and high-temperature stability. In this study, Al-Ni-Cu alloy powder was subjected to selective laser melting (SLM). The SLM Al-Ni-Cu alloy was manufactured using appropriate printing parameters, and its properties were investigated. The results revealed that the As-printed material exhibited a typical melting pool stack structure, with an ultimate tensile strength of 725 MPa but a high brittleness effect (low ductility). After traditional heat treatment, the melting pool structure did not completely disappear. The strengthening phase Al₇Cu₂₃Ni precipitated from the boundary of the melting pools; thus, the Al-Ni-Cu alloy maintained high strength (>500 MPa) and considerably increased ductility (>10%). The SLM Al-Ni-Cu alloy has considerable industrial application potential; therefore, increasing the heat treatment temperature or extending the heat treatment time in the future works can promote the decomposition of the melting pool boundary and solve the problem related to the aggregation behavior of the precipitation phase, thereby improving the fatigue life of the alloy.

Al–Mg–Sc–Zr alloy fabricated through selective laser melting (SLM) is an additive manufacturing alloy with promising industrial potential. In this study, as-printed specimens were subjected to either single-stage or two-stage heat treatment processes to investigate the effect of temperature from room temperature to high temperature on the specimens’ tensile and fatigue properties to establish a reliable reference for aerospace applications. The tensile test results indicated that the heat treatment contributed to determine the properties of the nanoprecipitate Al₃(Sc, Zr) with a strengthening phase, improving tensile strength. Moreover, the dynamics strain aging (DSA) effect vanished as temperature increased. It is noteworthy that the nanoprecipitation was distributed at the boundary of the melting pool after single-stage heat treatment with the highest tensile properties in all tests. In addition, the microstructure observed after the two-stage heat treatment indicated a melting pool interface decomposition, and the nanoprecipitation was homogeneously scattered over the Al matrix, increasing strength and further delaying fatigue crack transmission. Those features build a high-fatigue-resistance foundation. TEM analysis also confirmed the promotion of Sc thermal diffusion and an Al₃(Sc, Zr) precipitation transformation mechanism under two-stage heat treatment, corresponding to aforementioned inferences. The SLM Al–Mg–Sc–Zr alloy with two-stage heat treatment brings about balance between tensile properties and fatigue resistance, providing new insight into additive manufacturing with Al alloys.

Al-Si alloys exhibit promising wear resistance, thus being mainly employed to weld Al alloy parts and processed into components of equipment. During the new continuous casting direct rolling (CCDR) process, the raw material gradually cools and solidifies, simultaneously plastically deformed. Hence, the materials manufactured through the CCDR process presented an unparalleled microstructure. The experimental results indicated that the strength of the CCDR Al-Si alloy can be increased through cold rolling. A two-stage heat treatment (solid solution and aging treatment) was introduced to improve the ductility and satisfy the industrial application. Furthermore, the erosion wear characteristics and fracture mechanism of the CCDR Al-Si alloy dominated by the ductility were confirmed. Both cold rolling specimens (FR) and those with heat treatment (FRH) showed greater wear resistance than as-manufactured (F). The FR specimens exhibited greater wear resistance owing to a higher Al matrix strength at a lower impact angle; on the other hand, at a higher impact angle, the FRH specimens with a softer Al matrix presented better wear resistance due to the formation of a lip structure to reduce material removal. The TEM results confirmed that the nanoscale grains formation was induced in the erosion-affected region and affected the Si concentration. Conclusively, the heat-treated CCDR Al-Si alloy possessed excellent erosion resistance and workability, which can serve as a reference processed as wear-resistant mechanical parts.