Asphalt concrete has been widely used in road engineering as a surface material. Meanwhile, ultrasonic testing technology has also been developed rapidly. Aiming to evaluate the feasibility of the ultrasonic wave method, the present work reports a laboratory investigation on damage detection of asphalt concrete using piezo-ultrasonic wave technology. The gradation of AC-13 was selected and prepared based on the Marshall’s design. The ultrasonic wave velocities of samples were tested with different environmental conditions firstly. After that, the samples were destroyed into two types, one was drilled and the other was grooved. And the ultrasonic wave velocities of pretreated samples were tested again. Furthermore, the relationship between velocity and damaged process was evaluated based on three point bending test. The test results indicated that piezoelectric ultrasonic wave is a promising technology for damage detection of asphalt concrete with considerable benefits. The ultrasonic velocity decreases with the voidage increases. In a saturated water environment, the measured velocity of ultrasonic wave increased. In a dry environment (50 °C), the velocity the ultrasonic waves increased too. After two freeze-thaw cycles, the voidage increased and the ultrasonic velocity decreased gradually. After factitious damage, the wave must travel through or most likely around the damage, the ultrasonic velocity decreased. During the process of three point bending test, the ultrasonic velocity increased firstly and then decreased slowly until it entered into a steady phase. At last the velocity of ultrasonic wave decreased rapidly. In addition, the errors of the results under different test conditions need to be further studied.

Coalbed methane (CBM) is a kind of unconventional gas. CBM often contains a great deal of air when it comes out of the well. So, it must be condensed and purified before it can be applied. In this paper, raw clinoptilolite (Cp) was treated with grinding, gravimetric concentration, and ion-exchange using different aqueous solutions of salts. Then, the modified Cp powder was prepared into particles as adsorbents. Then, the adsorbents were used for nitrogen/methane separation in pressure swing adsorption (PSA) at the same condition of 0.2 MPa and 298 K. Research results indicated that there were micropores and lots of mesopores in the Cp, and the pores were mainly slit holes formed by sheet stacking. The adsorbents of NH₄-Cp, Cs-Cp, and Cu-Cp showed good equilibrium selectivity for CH₄, and the equilibrium separation factors of CH₄ and N₂ were 2.56, 2.31, and 1.95, respectively. The adsorbents of Na-Cp and Ag-Cp showed good equilibrium selectivity for N₂, and the equilibrium separation factors of N₂ and CH₄ were 7.25 and 6.53, respectively. Consequently, the adsorbent of Na-Cp was suitable for nitrogen/methane mixture separation, which could make the concentration of methane concentrated from 19.7% to 30.72%.