The current efforts in moving closer towards a circular plastics economy puts massive pressure on recycled plastics, especially recycled polyethylene (rPE) and recycled polypropylene (rPP) to enter new markets. Their market penetration remained low so far, despite PE and PP constituting the largest share of plastic wastes. However, with the current imperative of more circularity comes a new focus on performance of recyclates. Hence, a detailed understanding of composition and structure–property relationships of post-consumer recyclates has to be developed. Five recycling companies from the Austrian and German markets were asked to supply their purest high-quality rPE and rPP grades. These were characterized by differential scanning calorimetry (DSC), thermo-gravimetric analysis (TGA), and Fourier-transform infrared (FTIR) spectroscopy, and micro-imaging. Technological characterization included density measurements, determination of the melt flow rate (MFR), and Charpy impact testing. All recyclates contained diverse contaminants and inclusions ranging from legacy fillers like calcium carbonate to polymeric contaminants like polyamides or polyolefin cross-contamination. The overall amount, size, and distribution of contaminants varied significantly among suppliers. Furthermore, first structure–property relationships for polyolefin recyclates that link inorganic content and polymeric purity with density and impact performance could be derived.

At the moment, it looks like the plastics recycling industry is skimming only low-hanging fruits of its business. To reach intended targets, a greater effort and disruptive innovations are necessary. Physical- or digital-information-based solutions for tracking plastic material can support the circular economy and help to overcome hurdles along the value chain. In this paper, the scientific literature and initiatives in four different technology areas for information-based tracking solutions are reviewed and analyzed. Physical markers can improve sorting efficiencies on short notice but adhere some technical difficulties. Blockchain as a new concept promises high transparency and security, with the drawbacks of energy-intense verification and technical uncertainties. As a third group, the digital product passport claims a combination of physical and digital solutions with open questions on data ownership. The fourth and last group includes standards and certification systems that aim for maximum consensus with slow market implementation. To enable an integrated circular economy of plastics, plastic material tracking solutions must experience broad acceptance by all players along the value chain in the plastics industry and they should additionally be supported by society.

To enable the use of recyclates in thermoformed polypropylene products with acceptable optical appearance and good mechanical stability, a multilayer structure of virgin and recycled material can be used. When producing multilayer films with more than two layers, the used materials should have similar melt flow properties to prevent processing instabilities. In the case of a three-layer film, post-consumer recyclates are often hidden in the core layer. Due to the inconsistent melt flow properties of post-consumer recyclates, the adjustment of the melt flow properties of the core layer to those of the outer layers has to be realized by blending with virgin materials. In order to understand the effect of mixing with a virgin material with a certain pre-defined melt flow rate (MFR), material mixtures with different mixing partners from various sources were realized in this study. Hence, the pre-defined virgin material was mixed with (i) virgin materials, (ii) artificial recyclates out of a mixture of different virgin materials, and (iii) commercially available recyclates. These blends with mixing partner contents ranging from 0–100% in 10% increments were prepared by compounding and the MFR of each mixture was determined. For a mathematical description of the mixing behavior and furthermore for a proper MFR prediction of the material mix, existing mixing rules were tested on the three pre-defined sample groups. Therefore, this paper shows the applicability of different mixing rules for the prediction of the MFR of material blends. Furthermore, a new mixing rule was developed using symbolic regression based on genetic programming, which proved to be the most accurate predictive model.

This study demonstrates an open-loop recycling process of a specific post-consumer plastic waste stream. The targeted input waste material was defined as high-density polyethylene beverage bottle caps. Two methods of waste collection, informal and formal, were employed. Thereafter, materials were hand-sorted, shredded, regranulated, and then injection-molded into a flying disc (i.e., frisbee) as a pilot product. To observe the potential changes in the material throughout the entire recycling process, eight different test methods including melt mass-flow rate (MFR), differential scanning calorimetry (DSC), and mechanical tests were carried out on the various material states. The study showed that the informal collection led to a relatively higher purity in the input stream, which also appeared to have a 23% lower MFR value compared to that of the formally collected materials. The DSC measurements revealed a cross-contamination by polypropylene, which clearly affected the properties of all investigated materials. The cross-contamination led to a slightly higher tensile modulus in the recyclate, while the Charpy notched impact strength declined after processing by approximately 15% and 8% compared to those of the informal and formal input materials, respectively. All materials and the processing data were documented and stored online as a practical implementation of a digital product passport as a potential digital traceability tool. Furthermore, the suitability of the resulting recyclate to be used in transport packaging applications was also investigated. It was found that a direct replacement of virgin materials for this specific application is not possible without proper material modification.

Polypropylene (PP) plastic packaging waste consists of a variety of different plastic packaging products with a great span in rheological and mechanical behavior. Therefore, the resulting post-consumer recyclates usually show melt mass-flow rates (MFR) in the region of injection molding grades and intermediate mechanical properties. High-quality packaging applications demand a distinct property profile that is met by tailor-made PP grades and cannot be met by recyclates with intermediate performance. One such application with high market volume is high-stiffness thermoforming trays. The aim of this research was to blend intermediate-performance recyclates with a virgin PP grade to obtain compounds that fulfill the rheological and mechanical demands of this application. Three commercially available PP post-consumer recyclates were acquired and compounded with different blending ratios with a high stiffness, low MFR virgin PP grade. As the pure recyclates show different rheological properties, the blending ratios had to be adapted for each of them to fit into the MFR range of 2–4 g/10 min which is desirable for thermoforming applications. The resulting PP recyclate compounds show a distinct correlation of recyclate content with rheological and mechanical performance. However, the resulting property profile was directly dependent on the performance of the originally used recyclate. The best-performing recyclate could be used in a blending ratio of 65 m% recyclate content while adhering to both property limits, the MFR of 2–4 g/10 min and the lower bound tensile stiffness of 1500 MPa.

Post-consumer recyclates often have a property profile that results from mixing a variety of products, which are made from different materials, produced by different processing methods, and coming from applications with different lifetimes. This usually leads to a mixture of all these material properties in the recycling process. In contrast, virgin materials are specifically designed for applications and thus offer all the necessary properties for the intended products. In order to be able to use recycled materials for specific and demanding applications, not only the viscosity, which is important for processing and often varies greatly with recyclates, but also the mechanical properties, particularly the tensile modulus and impact strength, must be adjusted. For this purpose, various virgin materials of polypropylene homopolymers, random copolymers, and block copolymers with different flowabilities were mixed in different proportions and their properties were determined. The flowability of homopolymers and random copolymers in the blend behaved very similarly, while block copolymers exhibited a different behavior in some cases. By incorporating homopolymers into blends, the stiffness of the resulting material blend can be very well adjusted. The addition of random copolymers can increase strain at break, and the addition of block copolymers results in a significant increase in impact strength. In numbers, the maximum adjustment range for tensile modulus, yield stress, strain at break, and impact strength are 880 MPa, 14 MPa, 185%, and 6.9 kJ/m², respectively. While a good and reliable prediction of property profile is possible for polymer blends with different virgin materials, the resulting material properties for polymer blends of virgin and recycled materials are also influenced by impurities. In this work, however, a good prediction was also achieved for recyclate blends.