Surface modification of carbon fibers (CFs) is a critical step in preparing carbon fiber-reinforced composites. This study developed a continuous experimental process that integrates electrochemical anodic oxidation and chemical vapor deposition to fabricate carbon nanotubes/carbon fiber (CNTs/CF) reinforcements. The effects of temperature and hydrogen flow rate during CNT growth on the resulting reinforcements were systematically investigated. The surface morphology and mechanical properties of the modified materials were characterized using scanning electron microscopy, Raman spectroscopy, and single-fiber tensile testing. Employing an Fe_0.5Ni_0.5 bimetallic catalyst under optimized conditions (550 °C, H₂ flow rate: 0.45 mol/min, C₂H₂ flow rate: 0.30 mol/min), the resulting reinforcement exhibited an 8.7% increase in tensile strength compared to as-received CF.

Powder coating, as a promising coating material, has attracted widespread attention due to its convenient construction and being a green option, promoting environmental protection. However, the existence of defects such as insufficient leveling and poor mechanical properties of the coating during the coating process limits the further expansion of its application fields. Therefore, for this article, powder coatings with high leveling performance were prepared by composite modification of nylon 12 (PA-12) resin with polyacrylates and ethylene-α-olefin copolymers (POE). The introduction of modified polyacrylates reduces the surface tension of nylon chains, enhancing melt flowability during curing and making the coating surface smooth. Furthermore, by introducing POE, the flexibility of the powder coating was improved, and its fracture elongation increased from 59% for pure PA-12 to a maximum of 234%. This study provides an effective method for the modification of nylon powder coatings and offers new insights into their use in high-performance coating applications.