With increased awareness of environmental protection, the output of traditional curing agents such as cement and lime is less and less, so it is urgent to develop new curing agents with high efficiency and environmental benefits. Thus, this study aims at investigating the application of rice husk ash (RHA) from agricultural waste to the soft soil stabilization. A series of tests are conducted to analyze the strength development process and soil–water characteristics of rice husk ash–lime (RHA–lime) stabilized soils. The results of the strength tests showed that by increasing the content of RHA, the unconfined compressive strength (UCS) and splitting strength of stabilized soils increased first and then decreased. The effective shear strength indexes of the three soil types (soft soil, lime-stabilized soil, and RHA–lime soil) are measured and compared. It is found that RHA can effectively improve the shear resistance and water resistance of stabilized soil. The results of methylene blue test demonstrated that RHA can also promote the reduction of the specific surface area and swelling potential energy of lime-stabilized soil. In addition, the influence of RHA on mineral composition and morphology change in stabilized soils is studied at the microscopic level. The X-ray diffraction tests and scanning electron microscope (SEM) tests showed that strength development and change of soil–water properties of RHA–lime stabilized soil are attributed to enhanced cohesion by cementation and pores filling with agglomerated mineral.

Herein, the mechanical properties and carbonation durability of engineered cementitious composites (ECC) were studied. For the cost-efficient utilization of ECC materials, different types of specimens were cast with polypropylene (PP) and hydrophilic polyvinyl alcohol (HPVA) fibers. The compressive strength, Poisson’s ratio, strength-deflection curves, cracking/post-cracking strength, impact index, and tensile strain-stress curves of two types of ECC materials, with differing fiber contents of 0 vol %, 1 vol %, 1.5 vol %, and 2 vol %, were investigated with the use of compressive tests, four-point bending tests, drop-weight tests, and uniaxial tensile tests. In addition, the matrix microstructure and failure morphology of the fiber in the ECC materials were studied by scanning electron microscopy (SEM) analysis. Furthermore, carbonation tests and characterization of steel corrosion after carbonization were employed to study durability resistance. The results indicated that for both PP fiber- and HPVA fiber-reinforced ECCs, the compressive strength first increases and then decreases as fiber content increases from 0 vol % to 2 vol %, reaching a maximum at 1 vol % fiber content. The bending strength, deformation capacity, and impact resistance show significant improvement with increasing fiber content. The ECC material reinforced with 2 vol % PP fiber shows superior carbonized durability with a maximum carbonation depth of only 0.8 mm.

The recovery property of asphalt binders plays an important role in the performance and service life of asphalt pavements. Since the internal stress is the driving force for the recovery of asphalt binders, the accurate measurement of the internal stress is full of significance. Based on this rationale, this paper aims to measure the internal stress of asphalt binders using a creep and step-loading recovery (CSR) test and characterizing the recovery behaviors by the internal stress. One base asphalt binder and one styrene–butadiene–styrene (SBS)-modified binder are selected in this study. The key elements of the CSR test are carefully designed and its accuracy is verified in three aspects, including the loading conditions, the effect of disturbance by step-loads, and accuracy of measured internal stress. Then, a kinetics-based recovery model is proposed to evaluate and predict the recovery properties of asphalt binders from its causal relationship. The constant-rate recovery activation energy indicates a major difference with nondestructive and destructive loading conditions, while the fast-rate recovery activation energy keeps almost constant regardless of the loading conditions. After that, the healing activation energy is calculated by using the kinetics-based recovery model and the results indicate that SBS modified asphalt binder shows better healing abilities than a base binder.