Cellulose fiber-based textiles are ubiquitous in daily life for their processability, biodegradability, and outstanding flexibility. Integrating cellulose textiles with functional coating materials can unlock their potential functionalities to engage diverse applications. Metal-organic frameworks (MOFs) are ideal candidate materials for such integration, thanks to their unique merits, such as large specific surface area, tunable pore size, and species diversity. However, achieving scalable fabrication of MOFs-textiles with high mechanical durability remains challenging. Here, we report a facile and scalable strategy for direct MOF growth on cotton fibers grafted via the diazonium chemistry. The as-prepared ZIF-67-Cotton textile (ZIF-67-CT) exhibits excellent ultraviolet (UV) resistance and organic contamination degradation via the peroxymonosulfate activation. The ZIF-67-CT is also used to encapsulate essential oils such as carvacrol to enable antibacterial activity against E. coli and S. aureus. Additionally, by directly tethering a hydrophobic molecular layer onto the MOF-coated surface, superhydrophobic ZIF-67-CT is achieved with excellent self-cleaning, antifouling, and oil-water separation performances. More importantly, the reported strategy is generic and applicable to other MOFs and cellulose fiber-based materials, and various large-scale multi-functional MOFs-textiles can be successfully manufactured, resulting in vast applications in wastewater purification, fragrance industry, and outdoor gears.

In this study, fluorinated polycaprolactone (PCL) block polymers with different fluorine contents were synthesized via atom transfer radical polymerization (ATRP). An electrospraying technique was used to prepare fluorinated PCL microspheres with different microstructures. In contrast to the golf ball shape of unmodified PCL microspheres displaying porous pits on the surface, block polymer PCL-PTFOA(2 h) and PCL-PTFOA(6 h) microsphere surfaces displayed regular honeycomb-like pore structures. Thermally induced and evaporation-induced phase separations are proposed as the main mechanisms involved in the formation of the porous microstructures. The micro-phase separation between the two blocks of the fluorinated PCL copolymer is another factor that promoted the uniform collapse on the microsphere surface and the formation of its rugged wall. The surface roughness of the porous microspheres significantly improved their hydrophobicity, generating coating contact angles on aluminium foil substrates that measured as high as 162.4 ± 1.5°, which revealed that the surfaces were super-hydrophobic. Lastly, cotton fabric was directly coated with the fluorinated polymer microspheres via electrospraying, resulting in super-hydrophobic surfaces and CAs reaching 160.0 ± 1.3°. The results demonstrate that electrospraying is a simple, innovative and cost-effective method for preparing polymer microspheres with controllable microstructures for fabric coating applications.