We present a low-loss fan-in/fan-out (FIFO) device fabricated from a bundle of chemically etched optical fibers integrated within a standard FC/PC connector. The device demonstrates efficient coupling with insertion losses of 0.32 dB and 0.40 dB at wavelengths of 1310 nm and 1550 nm, respectively. Crosstalk and back reflection were measured to be below −41.8 dB and 51.3 dB, confirming high channel isolation and minimal signal degradation. This compact and connectorized solution offers a practical approach for scalable multicore fiber interfacing in advanced optical communication systems.

The present study introduces a novel design for lensed, chemically etched optical fibers (LEOFs) designed for efficient coupling with multicore fibers (MCFs). Experimental characterization at a wavelength of 1550 nm yielded an average coupling loss of approximately 0.76 dB under direct physical contact and 0.40 dB when the fiber end was positioned at an optimal working distance. Moreover, it was experimentally demonstrated that LEOFs exhibit high tolerance to longitudinal displacement and minimal wavelength-dependent variation in coupling efficiency. Based on this approach, fiber-in–fiber-out (FIFO) multicore couplers were fabricated using bundles of LEOFs that had been aligned to MCF cores. Bidirectional measurements yielded average insertion losses of 3.23–3.30 dB in TX and 3.20–3.27 dB in RX transmission directions at 1550 nm, with core-resolved losses as low as 1.09 dB for well-aligned channels. The results confirm the viability of LEOF-based multicore free-space coupling, with further improvements expected from enhanced fabrication accuracy.