In order to improve oil recovery efficiency in low-permeability reservoirs, this study developed amphiphilic Janus-SiO₂ nanoparticles to prepare polymer gel microspheres for enhanced oil recovery (EOR). Firstly, Janus-SiO₂ nanoparticles were synthesized via surface modification using (3-aminopropyl)triethoxysilane and α-bromoisobutyryl bromide. Fourier-transform infrared spectroscopy (FTIR) and scanning electron microscopy (SEM) characterization confirmed the successful grafting of amino and styrene chains, with the particle size increasing from 23.8 nm to 32.9 nm while maintaining good dispersion stability. The Janus nanoparticles exhibited high interfacial activity, reducing the oil–water interfacial tension to 0.095 mN/m and converting the rock surface wettability from oil-wet (15.4°) to strongly water-wet (120.6°), thereby significantly enhancing the oil stripping efficiency. Then, polymer gel microspheres were prepared by reversed-phase emulsion polymerization using Janus-SiO₂ nanoparticles as emulsifiers. When the concentration range of nanoparticles was 0.1–0.5 wt%, the particle size range of polymer gel microspheres was 316.4–562.7 nm. Polymer gel microspheres prepared with a high concentration of Janus-SiO₂ nanoparticles can ensure the moderate swelling capacity of the particles under high-temperature and high-salinity conditions. At the same time, it can also improve the mechanical strength and shear resistance of the microspheres. Core displacement experiments confirmed the dual synergistic effect of this system. Polymer gel microspheres can effectively plug high-permeability zones and improve sweep volume, while Janus-SiO₂ nanoparticles enhance oil displacement efficiency. Ultimately, this system achieved an incremental oil recovery of 19.72%, exceeding that of conventional polymer microsphere systems by more than 5.96%. The proposed method provides a promising strategy for improving oil recovery in low-permeability heterogeneous reservoir development.

To address scaling issues in oilfield water injection, a degradable terpolymer scale inhibitor MA-AA-AMPS (terpolymer)was synthesized via aqueous solution polymerization using maleic anhydride, acrylic acid, and 2-acrylamido-2-methylpropanesulfonic acid as monomers. Characterization confirmed the presence of carboxyl, sulfonic, and amide groups in the copolymer with good thermal stability. Scale inhibition tests showed that at 2% dosage, its scale inhibition efficiency exceeded 80%, remaining above 80% in the pH range of 3–8 and over 50% at 150 °C, with excellent tolerance to high-calcium environments. Biodegradation tests revealed BOD₅/COD > 0.3, with a biodegradation rate exceeding 50% in 15 days and reaching 83.4% in 30 days, indicating environmental friendliness. This scale inhibitor effectively solves scaling problems in oilfield water injection systems.