This paper presented a double-open multidirectional forging with relatively few deformation passes and a uniform deformation. The constitutive equation and dynamic recrystallization model of the GH4169 superalloy were identified based on a thermal compression test and imported into Deform simulation software. The microstructure evolution law of GH4169 superalloy undergoing double-open multidirectional forging was simulated. The evolution of the recrystallization volume fraction and recrystallized grain size of the GH4169 superalloy during double-open multidirectional forging was obtained. Both higher temperatures and more passes were found to produce more complete recrystallization and smaller recrystallization grain size. At the maximum temperature studied, 1000 °C, with nine passes, the recrystallization volume fraction exceeded 95%, and the recrystallized grain size reached 3–5.5 µm.

Based on the Kirkaldy-Venugopalan model, a theoretical model for the phase transformation of USIBOR^® 1500 high strength steel was established, and a graph of the phase transformation kinetics of ferrite, pearlite, and bainite were plotted using the software MATLAB. Meanwhile, with the use of the software DYNAFORM, the thermal stamping process of an automobile collision avoidance beam was simulated. The phase transformation law of USIBOR^® 1500 high-strength steel during hot stamping was studied through a simulation of the phase transformation during the pressure holding quenching process. In combination with the continuous cooling transformation (CCT) curve, the cooling rate of quenching must be greater than 27 °C/s to ensure maximum martensite content in the final parts, and the final martensite content increases as the initial temperature of the sheet rises.