The carbothermic reduction of calcined magnesite in vacuum was studied. By thermodynamic analysis, the starting temperature of reduction reaction dropped from 2173K to 1523K when system pressure dropped from 1 atmosphere to 100 Pa. The experiments were carried out at different conditions under 10~100 Pa and the experimental results shown that the reduction extent of MgO improved by increasing the reaction temperature and time, the pellet forming pressure as well as adding fluoride as catalyst. The rate-determining step of carbothermic reduction process was gas diffusion with the apparent activation energy of 241.19~278.56 kJ/mol.

En este trabajo se estudia la reducción de óxido de magnesio. La influencia de la composición de las escorias y de la temperatura de reducción sobre el porcentaje de reducción de óxido de magnesio han sido discutidas, y asimismo se ha estudiado la cinética de la reducción del óxido de magnesio en escorias fundidas. Los resultados muestran que la reducción se incrementa al aumentar alguno de los siguientes factores: la proporción de Al2O3/SiO2, la adición de CaF2, la proporción molar de Si/2MgO y la temperatura de reacción. En general la reducción fue controlada por la transferencia de masa en la escoria con una energía aparente de 586 kJ mol-1.