Titanate nanotubes were synthesized and subjected to an ion exchange reaction with erbium salt aqueous solution to obtain titanate nanotubes exchanged with erbium (3+) ions. In order to evaluate the effects of the thermal treatment atmosphere on the structural and optical properties of erbium titanate nanotubes, we subjected them to heat treatment in air and argon atmospheres. For comparison, titanate nanotubes were also treated in the same conditions. A complete structural and optical characterizations of the samples was performed. The characterizations evidenced the preservation of the morphology with the presence of phases of erbium oxides decorating the surface of the nanotubes. Variations in the dimensions of the samples (diameter and interlamellar space) were promoted by the replacement of Na⁺ by Er³⁺ and the thermal treatment in different atmospheres. In addition, the optical properties were investigated by UV–Vis absorption spectroscopy and photoluminescence spectroscopy. The results revealed that the band gap of the samples depends on the variation of diameter and sodium content caused by ion exchange and thermal treatment. Furthermore, the luminescence strongly depended on vacancies, evidenced mainly by the calcined erbium titanate nanotubes in argon atmosphere. The presence of these vacancies was confirmed by the determination of Urbach energy. The results suggest the use of thermal treated erbium titanate nanotubes in argon atmosphere in optoelectronics and photonics applications, such as photoluminescent devices, displays, and lasers.

This work reports the functionalization of sodium titanate nanotubes with amine groups obtained from the reaction of titanate nanotubes with [3-(2-Aminoethylamino)propyl]trimethoxysilane, NaTiNT−2NH, and 3-[2-(2-Aminoethylamino)ethylamino]propyltrimethoxysilane, NaTiNT−3NH. It was verified that the crystalline and morphological structures of NaTiNT were preserved after the functionalization, spectroscopies showed that aminosilane interacted covalently with the surface of NaTiNT, and the incorporation of the aminosilane groups on the surface of NaTiNT can be confirmed. The adsorbent matrices NaTiNT−2NH and NaTiNT−3NH were used to remove the anionic dye from remazol blue R (RB) in aqueous medium, and the highest adsorption capacity was around 365.84 mg g${}^{-1}$ (NaTiNT−2NH) and 440.70 mg g${}^{-1}$ (NaTiNT−3NH) in the range of pH 5.0 to 10.0 and the equilibrium time was reached in 210 min (NaTiNT−2NH) and 270 min (NaTiNT−3NH). Furthermore, the Elovich model, which reports the adsorption in heterogeneous sites and with different activation energies in the chemisorption process, was the most appropriate to describe the adsorption kinetics. Thus, these adsorbent matrices can be used as an alternative potential for dye removal RB in aqueous solution.

Strategies for the production of new nanocomposites that promote bone tissue regeneration are important, particularly those that enhance the osteoinduction of hydroxyapatite in situ. Here, we studied and report the synthesis of nanohydroxyapatite and titanate nanotube (nHAp/TiNT) composites formulated at different concentrations (1, 2, 3, and 10 wt % TiNT) by means of a wet aqueous chemical reaction. The addition of TiNT affects the morphology of the nanocomposites, decreasing the average crystallite size from 54 nm (nHAp) to 34 nm (nHAp/TiNT10%), while confirming its interaction with the nanocomposite. The crystallinity index (CI) calculated by Raman spectroscopy and XRD showed that the values decreased according to the increase in TiNT concentration, which confirmed their addition to the structure of the nanocomposite. SEM images showed the presence of TiNTs in the nanocomposite. We further verified the potential cytotoxicity of murine fibroblast cell line L929, revealing that there was no remarkable cell death at any of the concentrations tested. In vivo regenerative activity was performed using oophorectomized animal (rat) models organized into seven groups containing five animals each over two experimental periods (15 and 30 days), with bone regeneration occurring in all groups tested within 30 days; however, the nHAp/TiNT10% group showed statistically greater tissue repair, compared to the untreated control group. Thus, the results of this study demonstrate that the presently formulated nHAp/TiNT nanocomposites are promising for numerous improved bone tissue regeneration applications.