This study evaluated non-fibrous Mg-clays as potential adsorbents of emerging contaminants (ECs) from water. The materials were characterized, and their textural and structural properties were related to their ability to remove two model EC molecules: ciprofloxacin (CPX) and lidocaine (LID). The results showed that Ad-6 and Ad-7 are mixed-layer kerolite/stevensite, while Ad-5 and Ad-8 are mainly composed of smectite minerals like stevensite and saponite, respectively. Ad-8 exhibited the highest CPX-adsorption capacity (0.91 mmol·g⁻¹ clay), likely due to its saponite content. Mixed-layer materials also performed well, with Ad-6 and Ad-7 achieving an adsorption capacity of 0.8 and 0.55 mmol·g⁻¹ clay, respectively. Adsorption studies suggested that CPX is adsorbed through ion exchange in materials with high smectite content (Ad-8 and Ad-5), while interstratified materials showed enhanced retention due to kerolite presence, which improves their porous structures. Similar findings were observed for LID, indicating a cationic-exchange mechanism for LID adsorption in all the materials and suggesting that the molecular size of the EC could regulate the removal capacity of these materials. This work showed that the studied Mg-clays could be effectively used for the removal of pharmaceutical pollutants, expanding their commercial possibilities.

Adsorption studies of ciprofloxacine (CPX) and lidocaine (LID) emerging contaminants were performed on two fibrous Mg clays from the Madrid basin and Senegal. The samples were characterized by X-ray diffraction, ICP major element analysis, infrared spectroscopy, thermal analysis, optical petrography, scanning and transmission electron microscopy, cation exchange capacity (CEC), and N₂-BET analysis. Two mineral assemblages were established. Assemblage 1 mainly consists of sepiolite and minor trioctahedral smectite, while assemblage 2 is mostly composed of palygorskite, which is associated with dioctahedral smectite. The sorption was fast and reached equilibrium in 2 h. Fibrous Mg clays showed a higher adsorption capacity for CPX than for LID in the conditions studied. CPX adsorption on sepiolite and palygorskite can be the result of the combination of various mechanisms: ion exchange with permanently charged sites, electrostatic attractions with external surfaces, and an inner sphere complex with broken edges. LID adsorption mainly occurs by ion exchange and electrostatic interaction with the external surfaces of the clays. Dioctahedral smectite, as an associated phase, contributed to a higher removal percentage in palygorskite samples. By contrast, the trioctahedral smectite did not play a significant role in the adsorption of the samples with sepiolite. The mesoporous structure, high surface area, and moderate cation exchange of fibrous clays play a key role in the sorption process of CPX and LID.