Characterization studies conducted on Class-F fly-ash specimens gathered from different producers in the southeastern United States confirm general trends reported for fly ash worldwide. Additional tests and detailed analyses explain the spread in specific gravity (interparticle porosity cenospheres), highlight the tendency to segregation and layering, and show marked ferromagnetism. Furthermore, data show that early diagenetic cementation—within days after wetting—hinders densification and produces a fabric that is prone to collapse. New procedures are specifically developed to diagnose and characterize early diagenesis, including (1) pH measurements as an indicator of diagenetic potential, (2) test protocols to assess early diagenesis using oedometer tests and shear-wave velocity, and (3) procedures to determine realizable unit weights as reference values for the analyses of contractive or dilative tendencies and instability. In the absence of early diagenetic cementation, dilative fly-ash behavior is expected in the upper $\approx 20\mathrm{m}$ under monotonic shear loading. Flow instability may follow the failure of the containment structure if the ponded ash is saturated and has experienced hindered densification.

In cryogenic fracturing, a rock surface exposed to cryogenic fluids undergoes a large thermal gradient, and the resultant local tensile stress overcomes rock strength and initiates fractures. This study investigates the development of cracks generated from the cryogenic treatment of a borehole under no external confining stress on specimens. The experiments were performed on transparent PMMA specimens to observe fracture proliferation around boreholes. Liquid nitrogen was flowed through the boreholes to cool the borehole surface. The results show that initial fracture growth is characterized by abrupt starts and stops, and as the fracture propagates outward, the growth appears more continuous. In an early stage, horizontal/radial fractures and vertical fractures are the defining patterns. Horizontal fractures tend to be separated by a specific exclusion distance (i.e., spacing between cracks). While distinct horizontal/vertical fractures and exclusion distance manifest themselves at an early stage, fractures resulting from fracture interactions and curvatures can develop into complex shapes at later stages. Cryogenic thermal loading induces distinctively curved fractures. The tendency of curvature may prevent greater penetration. An increase in the borehole pressure during liquid nitrogen flow, however, can lessen fracture tortuosity and facilitate radial propagation. A high flow pressure and rate are also advantageous in that they accelerate cooling and fracture propagation.