This review presents a thorough analysis of the research and future development of particle electrodes used for catalyzing pollutants in electrochemical systems.

Sodium dodecyl sulfate stable nanoscale zero-valent iron (SDS-nZVI) was synthesized by the sodium borohydride reduction method, characterized with SEM and XRD. SDS-nZVI was used for the removal of Cr (VI) from aqueous solutions at different conditions in a batch process. XRD analysis indicated the presence of iron oxide and iron-chromium hydroxide coprecipitation on the surface of SDS-nZVI after reaction some time. The reaction kinetics, mechanism, isotherms, and thermodynamics for Cr (VI) removal of aqueous solution via SDS-nZVI were investigated. The pseudo-second-order model was relatively suitable for describing the reaction process. Intraparticle diffusion model was used to analysis the mechanism, the results indicated that there were two processes (bulk diffusion and surface diffusion) controlling the reaction rate, while only one was rate limiting in any particular time range. The fitted Temkin and D-R model satisfactorily explanted the experimental data in the range of 303–343 K. The maximum removal capacity of SDS-nZVI for Cr (VI) was obtained for 336.7 mg g⁻¹ at 303 K. The overall removal process was endothermic. These results demonstrated that SDS-nZVI could potentially be used as an effective material for environmental remediation.

Fe-doped TiO₂nanotubes (Fe-TNTs) have been prepared by ultrasonic-assisted hydrothermal method. The structure and composition of the as-prepared TiO₂nanotubes were characterized by transmission electron microscopy, X-ray diffraction, and UV-Visible absorption spectroscopy. Their photocatalytic activities were evaluated by the degradation of MO under visible light. The UV-visible absorption spectra of the Fe-TNT showed a red shift and an enhancement of the absorption in the visible region compared to the pure TNT. The Fe-TNTs were provided with good photocatalytic activities and photostability and under visible light irradiation, and the optimum molar ratio of Ti : Fe was found to be 100 : 1 in our experiments.