Substrate topography can have profound effects on initial bacterial adhesion during biofilm formation. We applied Staphylococcus epidermidis and Escherichia coli cells onto periodically structured substrates with different structure dimensions, structure types and wetting properties. We found a strong dependence of cell retention on the structure dimensions of the applied substrates. Periodicities in the range of the cell size increased, whereas smaller periodicities decreased cell retention, independent of contact time (minutes to hours) and hydrophobicity. These novel insights on the role of surface topography on bacterial retention might facilitate the development of non-fouling surfaces in the future.

Fabricating aluminium surfaces with superhydrophobic and ice-repellent properties present nowadays a challenging task. In this work, multifunctional structures are manufactured by direct laser writing and direct laser interference patterning methods using pulsed infrared laser radiation (1064 nm). Different periodic patterns with feature sizes ranging from 7.0 to 50.0 µm are produced. In addition, hierarchical textures are produced combining both mentioned laser based methods. Water contact angle tests at room temperature showed that all produced patterns reached the superhydrophobic state after 13 to 16 days. In addition, these experiments were repeated at substrate temperatures from −30 °C to 80 °C allowing to determine three wettability behaviours as a function of the temperature. The patterned surfaces also showed ice-repellent properties characterized by a near three-fold increase in the droplets freezing times compared to the untreated samples. Using finite element simulations, it was found that the main reason behind the ice-prevention is the change in the droplet geometrical shape due to the hydrophobic nature of the treated surfaces. Finally, dynamic tests of droplets imping the treated aluminium surfaces cooled down to −20 °C revealed that only on the hierarchically patterned surface, the droplets were able to bounce off the substrate.

Interfering laser beams of a high-power pulsed laser provide the opportunity of applying a direct lateral interaction with the surface microstructure of metals in micro/nano-scale based on photo-thermal nature mechanisms. This “Laser interference metallurgy” allows the creation of periodic patterns of features with a well defined long-range order on metallic surfaces at the scale of typical microstructures (from the sub micrometer level up to micrometers). This technique is an approach to initiate metallurgical processes such as melting, recrystallization, recovery, and defect and phase formation in the lateral scale of the microstructure itself and with an additional long range order given by the interference periodicity. In this work, the laser interference theory is described and used to calculate multi-beam interference patterns. A method to calculate the numbers of laser beams as well as the geometrical arrangement of the beams to obtain a desired periodical pattern prior to experiments is presented. The formation of long-range-ordered intermetallic compounds as well as macroscopic and microscopic variations of mechanical properties on structured metallic thin films are presented as examples.