Noble Metal-free catalysts attracted much attention as promising candidates for Pt-based catalyst replacement to advance applications related to oxygen reduction reaction (ORR), which is critical for large-scale renewable energy storage and conversion. Herein, this work focused on a synthesis of noble metal-free ORR electrocatalysts consisting of porous N-rich carbon/MXene, which was obtained using very conductive and reactive Ti₃C₂ MXene and polypyrrole (PPy) as a C and N source. The electrocatalyst exhibited excellent electrocatalytic activity and stability with an onset and a half-wave potentials equal to 0.85 and 0.71 V, respectively. Results obtained in this work demonstrate how to design efficient noble metal-free ORR electrocatalysts applicable to other chemical systems.

The effect of single-layer graphene sheets (Gr) on the corrosion protection of zinc-rich epoxy primers (ZRPs) was investigated. Scanning electron microscopy (SEM) with an energy dispersive spectrometer (EDS) were used to characterize morphology and composition of the coatings after immersion for 25 days. The cross-sectional SEM images and X-ray photoelectron spectroscopy (XPS) confirmed that the addition of single-layer graphene facilitated assembling of zinc oxides on the interface between the coating and the steel. The open circuit potential (OCP), electrochemical impedance spectroscopy (EIS) measurements revealed that both the cathodic protection and barrier performance of the ZRP were enhanced after addition of 0.6 wt. % Gr (Gr0.6-ZRP). In addition, the cathodic protection property of the Gr0.6-ZRP was characterized quantitatively by localized electrochemical impedance spectroscopy (LEIS) in the presence of an artificial scratch on the coating. The results demonstrate that moderate amounts of single-layer graphene can significantly improve corrosion resistance of ZRP, due to the barrier protection and cathodic protection effects.

The corrosion behavior of zinc-rich epoxy primers or paints (ZRPs) with different conducting polyaniline-grafted graphene (PANI/Gr) contents was investigated. Conductivity of the formed PANI/Gr nanosheets was significantly improved by employing the Gr as the inner template to synthesize the PANI. The protective properties and electrochemical behavior of coatings with artificial defects were investigated by monitoring the free corrosion potential versus time and by using localized electrochemical impedance spectroscopy (LEIS). A synergetic enhancement of the physical barrier role of the coating and the zinc sacrificial cathodic protection was achieved in the case of ZRP including PANI/Gr nanosheets. In addition, the ZRP mixed with the PANI/Gr at a content of 0.6% exhibited the best anticorrosion performance across the range of investigated PANI/Gr contents.