This study aims to prepare bamboo-fiber-reinforced cement composites and provide a solution to the issue of poor interfacial adhesion between bamboo fibers and cement matrix. The original bamboo fibers were modified by three moderately low-cost and easy-to-handle treatments including glycerol, aluminate ester, and silane treatments. The performance of the modified bamboo-fiber-reinforced cement composites was evaluated by a series of mechanical and durability tests, including flexural and compressive strength, water absorption, chloride ion penetration, drying shrinkage, freeze–thaw resistance, and carbonization. In addition, the microstructures of composites were characterized using a scanning electron microscope (SEM). The results showed that the composites reinforced with glycerol-modified bamboo fibers had 14% increased flexural strength and comparable compressive strength. From durability perspectives, all treatments showed similar performance in drying shrinkage, whereas aluminate ester treatment was the most effective in terms of impermeability, chloride resistance, freeze–thaw resistance, and carbonization. The results could provide insights to efficient and effective natural fiber treatment to enable better performance of natural-fiber-reinforced cement-based materials.

The present work aimed at developing fully green composites from renewable materials, i.e., acrylated epoxidized soybean oil (AESO) and microcrystalline cellulose (MCC) by a solution casting method. The reinforcing effect of MCC on AESO resins was optimized by adjusting MCC loading from 20 to 40 wt % in terms of physical, mechanical, and thermal properties as well as water absorption of the resulting MCC/AESO composites. The interaction between MCC and AESO was characterized by Fourier transform infrared (FTIR) analysis, which revealed possible hydrogen bonds between the –OH groups of MCC along with the polar components of AESO including C=O, –OH, and epoxy groups. This was further evidenced by a benign interfacial adhesion between MCC and AESO resins as revealed by scanning electron microscope (SEM) analysis. The incorporation of MCC into AESO resins significantly increased the density, hardness, flexural strength, and flexural modulus of the MCC/AESO composites, indicative of a significant reinforcing effect of MCC on AESO resins. The composite with 30 wt % MCC obtained the highest physical and mechanical properties due to the good dispersion and interfacial interaction between MCC and AESO matrix; the density, hardness, flexural strength, and flexural modulus of the composite were 15.7%, 25.0%, 57.2%, and 129.7% higher than those of pure AESO resin, respectively. However, the water resistance at room temperature and 100 °C of the composites were dramatically decreased due to the inherent hydrophilicity of MCC.