A method to obtain long lengths of flexible, biaxially oriented substrates with smooth, chemically compatible surfaces for epitaxial growth of high‐temperature superconductors is reported. The technique uses well established, industrially scalable, thermomechanical processes to impart a strong biaxial texture to a base metal. This is followed by vapor deposition of epitaxial buffer layers (metal and/or ceramic) to yield chemically compatible surfaces. Epitaxial YBa₂Cu₃O_x films grown on such substrates have critical current densities exceeding 10⁵ A/cm² at 77 K in zero field and have field dependencies similar to epitaxial films on single crystal ceramic substrates. Deposited conductors made using this technique offer a potential route for the fabrication of long lengths of high‐J_c wire capable of carrying high currents in high magnetic fields and at elevated temperatures.

In-plane-aligned, c axis-oriented YBa ₂ Cu ₃ O ₇ (YBCO) films with superconducting critical current densities J _c as high as 700,000 amperes per square centimeter at 77 kelvin have been grown on thermomechanically rolled-textured nickel (001) tapes by pulsed-laser deposition. Epitaxial growth of oxide buffer layers directly on biaxially textured nickel, formed by recrystallization of cold-rolled pure nickel, made possible the growth of YBCO films 1.5 micrometers thick with superconducting properties that are comparable to those observed for epitaxial films on single-crystal oxide substrates. This result represents a viable approach for the production of long superconducting tapes for high-current, high-field applications at 77 kelvin.

We demonstrated short segments of a superconducting wire that meets or exceeds performance requirements for many large-scale applications of high-temperature superconducting materials, especially those requiring a high supercurrent and/or a high engineering critical current density in applied magnetic fields. The performance requirements for these varied applications were met in 3-micrometer-thick YBa ₂ Cu ₃ O _7-δ films epitaxially grown via pulsed laser ablation on rolling assisted biaxially textured substrates. Enhancements of the critical current in self-field as well as excellent retention of this current in high applied magnetic fields were achieved in the thick films via incorporation of a periodic array of extended columnar defects, composed of self-aligned nanodots of nonsuperconducting material extending through the entire thickness of the film. These columnar defects are highly effective in pinning the superconducting vortices or flux lines, thereby resulting in the substantially enhanced performance of this wire.