Zirconia is a material that mimics human teeth and has been extensively studied and applied. This study investigated the surface modifications of dental zirconia induced by two UV-C wavelengths (222 and 254 nm). A total of 72 zirconia specimens were prepared and divided into groups for irradiation at varying distances (1, 6, 12 cm) and durations (40, 120, 480 and 1440 min), with three specimens retained as untreated controls. Surface changes were assessed by measuring colour difference (ΔE) and water contact angle, and by analyzing surface morphology and elemental composition using SEM and EDX, and XRD was employed to determine the crystalline structure. The results showed that both wavelengths induced clinically perceptible colour changes (ΔE > 2.0), with the most pronounced effect at 6 cm for 222 nm and 1 cm for 254 nm. WCA decreased significantly with irradiation time, showing a linear correlation with log(time), and 222 nm irradiation yielded lower WCA than 254 nm. While SEM revealed no morphological changes, both UV treatments significantly increased the Zr/O ratio compared to the control. XRD tests confirmed that UV-C irradiation does not damage the zirconium oxide crystal structure. It is concluded that both UV-C wavelengths can alter the colour and enhance the wettability of zirconia; these modifications are particularly relevant for dental restorative applications, specifically in the fabrication of anterior tooth crowns, where achieving a natural tooth-like appearance is desired.

UV-C irradiation enables digital zirconia colouring. This study investigates the atomic mechanism driving this defect-induced optical change. The band gap was calculated from the absorption spectra with the Tauc plot. The absorption spectra were measured using UV–visible spectroscopy. The surface composition was evaluated through X-ray photoelectron spectroscopy (XPS). The location of the oxygen vacancy was tested through electron paramagnetic resonance (EPR). The computer calculation using Density Functional Theory was conducted and the density of states (DOSs) were calculated. The band gap reduced rapidly from the baseline group (3.184 eV) to the 30 min irradiated group (3.097 eV). The XPS results showed that the electron density around O1s reduced and the electron density around Zr 3d increased. The EPR signal (g = 2.0037) increases progressively as the UV-C irradiation time is prolonged from 15 min to 24 h, indicating the accumulation of paramagnetic defect centres. The DOSs suggested the emergence of defect-associated states and band-edge tailing in oxygen deficient models, consistent with the experimentally observed reduction in the Tauc-derived optical band gap. This study confirmed the mechanism by which UV-C-induced oxygen vacancies modify the colour of 3Y-TZP.