The shear-induced transformations between oriented planar lamellae and a state of closely packed multilamellar vesicles (MLVs) in a lyotropic nonionic surfactant model system were studied by the combination of nuclear magnetic resonance (NMR) spectroscopy and diffusometry with magnetic resonance imaging (MRI). ²H NMR imaging confirmed the discontinuous nature of the transition from onions to planar lamellae, revealing the spatial coexistence of both states within the gap of the cylindrical Couette geometry. On the other hand, NMR diffusion measurements in three principal directions and at various values of strain strongly suggest that a multi-lamellar cylindrical or undulated intermediate structure exists during the continuous and spatially homogeneous transition from planar lamellae to MLVs

Thermally stabilized and subsequently carbonized nanofibers are a promising material for many technical applications in fields such as tissue engineering or energy storage. They can be obtained from a variety of different polymer precursors via electrospinning. While some methods have been tested for post-carbonization doping of nanofibers with the desired ingredients, very little is known about carbonization of blend nanofibers from two or more polymeric precursors. In this paper, we report on the preparation, thermal treatment and resulting properties of poly(acrylonitrile) (PAN)/poly(vinylidene fluoride) (PVDF) blend nanofibers produced by wire-based electrospinning of binary polymer solutions. Using a wide variety of spectroscopic, microscopic and thermal characterization methods, the chemical and morphological transition during oxidative stabilization (280 °C) and incipient carbonization (500 °C) was thoroughly investigated. Both PAN and PVDF precursor polymers were detected and analyzed qualitatively and quantitatively during all stages of thermal treatment. Compared to pure PAN nanofibers, the blend nanofibers showed increased fiber diameters, strong reduction of undesired morphological changes during oxidative stabilization and increased conductivity after carbonization.