Based on semi-solid mixing technology, two kinds of as-cast Grp (Graphite particles)/AZ91 composites with different Grp volume fractions (5 vol %, 10 vol %) were prepared; these are called 5 vol % Grp/AZ91 composites and 10 vol % Grp/AZ91 composites, respectively. In order to eliminate casting defects, refine grains, and improve mechanical properties, thermal deformation analysis of these composites was conducted. The effect of the addition of Grp and thermal deformation on the microstructure, mechanical properties, and wear resistance of AZ91 composite was explored. The results showed that after 5 vol % Grp was added into the as-cast AZ91 alloy, Mg₁₇Al₁₂ phases were no longer precipitated reticularly along the grain boundary, and Al₄C₃ phases were formed inside the composite. With the increase in the volume fraction of Grp, the grains of the AZ91 composites were steadily refined. With the increase of forging pass, the grain size of 5% Grp/AZ91 composites decreased first, and then increased. Additionally, the Grp size decreased gradually. There was little change in the yield strength, and the tensile strength and elongation were improved to a certain extent. After forging and extrusion of 5% Grp/AZ91 composites once, the grain size and Grp size were further reduced, and the yield strength, tensile strength, and elongation were increased by 23%, 30%, and 65%, respectively, compared with the composite after forging. With the increase of the number of forging passes before extrusion, the grain size decreased little by little, while the Grp size remained unchanged. The average yield strength, tensile strength, and elongation of the composites after forging and extrusion six times were increased by 3%, 3%, and 23%, respectively, compared with the composite after forging and extrusion once. The wear rate and friction coefficient of the 5% Grp/AZ91 composites decreased after forging once, and the wear mechanism was mainly due to ploughing wear. By comparison, the wear rate and friction coefficient of the 5% Grp/AZ91 composites increased in the extrusion state, and the main wear mechanism was from wedge formation and micro-cutting wear.

The present study investigated high-aspect ratio micro-hole array parts which were made by ZrO₂ micro-powder with different particle sizes and micro-powder injection molding technology. It analysed the influence of particle sizes on feedstock, debinding and sintering of ceramic nozzles with multi-micro-holes. The forming quality of ceramic nozzles with multi-micro-holes was discussed in this paper. The results show that the two mixed ZrO₂ feedstocks have fine uniformity. The average deviation of the feedstock made with 200 nm powder was −2%, and the average deviation of the feedstock made with 100 nm powder was −7.1%. The sample showed certain sintering characteristics which provided better strength (11.10 MPa) to parts after debinding. The linear shrinkage and the density of the two powder samples at different sintering temperatures increased as the sintering temperature increased. If the temperature continued to increase, the linear shrinkage and the density decreased. The highest hardness and flexural strength values of the ZrO₂ sample with 200 nm powder used were: 1265.5 HV and 453.4 MPa, and the crystalline particle size was 0.36 μm. The highest hardness and flexural strength values of the ZrO₂ sample with 100 nm powder used were: 1425.8 HV and 503.6 MPa, and the crystalline particle size was 0.18 μm. The ceramic nozzles with multi-micro holes shrunk to nearly the same axial, radial and circumferential directions during sintering. After sintering, the roundness of ceramic micro-hole met the user requirements, and the circular hole had a high parallelism in the axial direction. The micropore diameter was 450 ± 5 μm, and it was possible to control the dimensional accuracy within 1.5% after sintering. The study presented a superior application prospect for high-aspect ratio micro hole array parts in aerospace, electronics and biomedicine.