Selective laser melting (SLM) is a powder bed fusion type metal additive manufacturing process which is being applied to manufacture highly customised and value-added parts in biomedical, defence, aerospace, and automotive industries. Aluminium alloy is one of the widely used metals in manufacturing parts in SLM in these sectors due to its light weight, high strength, and corrosion resistance properties. Parts used in such applications can be subjected to severe dynamic loadings and high temperature conditions in service. It is important to understand the mechanical response of such products produced by SLM under different loading and operating conditions. This paper presents a comprehensive review of the latest research carried out in understanding the mechanical properties of aluminium alloys processed by SLM under static, dynamic, different build orientations, and heat treatment conditions with the aim of identifying research gaps and future research directions.

Selective Laser Melting (SLM) is a powder-bed type Additive Manufacturing (AM) process, where parts are built layer-by-layer by laser melting of powder layers of metal. There are several SLM process parameters that affect the accuracy and quality of the metal parts produced by SLM. Therefore, it is essential to understand the effect of these parameters on the quality and properties of the parts built by this process. In this paper, using Taguchi design of experiments, the effect of four SLM process parameters namely laser power, defocus distance, layer thickness and build orientation are considered on the porosity of 17-4PH stainless steel parts built on ProX200 SLM direct metal printer. The porositywas found to be optimum at a defocus distance of -4mm and a laser power of 240 W with a layer thickness of 30 μm and using vertical build orientation.