We present a simple method to coat microneedles (MNs) uniformly with a porous polymer (PLGA) that can deliver drugs at high rates. Stainless steel (SS) MNs of high mechanical strength were coated with a thin porous polymer layer to enhance their delivery rates. Additionally, to improve the interfacial adhesion between the polymer and MNs, the MN surface was modified by plasma treatment followed by dip coating with polyethyleneimine, a polymer with repeating amine units. The average failure load (the minimum force sufficient for detaching the polymer layer from the surface of SS) recorded for the modified surface coating was 25 N, whereas it was 2.2 N for the non-modified surface. Calcein dye was successfully delivered into porcine skin to a depth of 750 µm by the porous polymer-coated MNs, demonstrating that the developed MNs can pierce skin easily without deformation of MNs; additional skin penetration tests confirmed this finding. For visual comparison, rhodamine B dye was delivered using porous-coated and non-coated MNs in gelatin gel which showed that delivery with porous-coated MNs penetrate deeper when compared with non-coated MNs. Finally, lidocaine and rhodamine B dye were delivered in phosphate-buffered saline (PBS) medium by porous polymer-coated and non-coated MNs. For rhodamine B, drug delivery with the porous-coated MNs was five times higher than that with the non-coated MNs, whereas 25 times more lidocaine was delivered by the porous-coated MNs compared with the non-coated MNs.

This work demonstrates a simple approach for coating a porous polymer layer on stainless-steel (SS) microneedles characterized by a pH-responsive formulation for self-regulated drug delivery. For many drug-delivery applications, the release of therapeutic agents in an acidic microenvironment is desirable. Acid-sensitive polymers and hydrogels were extensively explored, but easily prepared polymeric microcarriers that combine acid sensitivity and biodegradability are rare. Here, we describe a simple and robust method of coating a porous polymer layer on SS microneedles (MNs) that release a model drug (lidocaine) in a pH-responsive fashion. It was constructed by packing the model drug and a pH-sensitive component (sodium bicarbonate) into the pores of the polymer layer. When this acid-sensitive formulation was exposed to the acidic microenvironment, the consequent reaction of protons (H⁺) with sodium bicarbonate (NaHCO₃) yielded CO₂. This effect generated pressure inside the pores of the coating and ruptured the thin polymer membrane, thereby releasing the encapsulated drug. Scanning electron micrographs showed that the pH-sensitive porous polymer-coated MNs exposed to phosphate-buffered saline (PBS) at pH 7.4 were characterized by closed pores. However, MNs exposed to PBS at pH 5.5 consisted of open pores and the thin membrane burst. The in vitro studies demonstrated the pH sensitivity of the drug release from porous polymer-coated MNs. Negligible release was observed for MNs in receiving media at pH 7.4. In contrast, significant release occurred when the MNs were exposed to acidic conditions (pH 5.5). Additionally, comparable results were obtained for drug release in vitro in porcine skin and in PBS. This revealed that our developed pH-responsive porous polymer-coated MNs could potentially be used for the controlled release of drug formulations in an acidic environment. Moreover, the stimuli-responsive drug carriers will enable on-demand controlled release profiles that may enhance therapeutic effectiveness and reduce systemic toxicity.

A closed-loop system imitating the function of pancreatic cells, connected to microneedles (MNs) that automatically “release” insulin in response to the blood glucose (BG) levels would be highly satisfactory for improving the quality of life and health for diabetes patients. This paper describes an easy, fast and simple technique of coating a porous polymer layer on stainless steel (SS) MNs that release insulin in a glucose-responsive fashion. It was fabricated by sealing insulin, sodium bicarbonate (a pH-sensitive element [NaHCO₃]) and glucose oxidase (glucose-specific enzymes [GOx]) into the pores of a porous polymer coating. Glucose can passively diffuse into the pores and become oxidized to gluconic acid by GOx, thereby causing a decrease in local pH. The subsequent reaction of protons with NaHCO₃ forms carbon dioxide (CO₂) which creates pressure inside the pores, thereby rupturing the thin polymer film and releasing the encapsulated insulin. Field emission scanning electron microscopy (FE-SEM) images displayed that upon the exposure of MNs to glucose-free phosphate buffer saline (PBS) with pH 7.4, the pores of the porous MNs were closed, while in MNs exposed to a hyperglycemic glucose level, the pores were opened and the thin film burst. These MNs demonstrated both in vitro (in porcine skin and PBS) and in vivo (in diabetic rats) glucose-mediated insulin release under hyperglycemic conditions with rapid responsiveness. This study validated that the release of insulin from porous MNs was effectively correlated with glucose concentration.

A new fabrication method of a polydimethylsiloxane (PDMS) stencil embedded microwell plate is proposed and applied to a localized culture of Purkinje neurons (PNs) and neural stem cells (NSCs). A microwell plate combines a PDMS stencil and well plate. The PDMS stencil was fabricated by spin casting from an SU-8 master mold. Gas blowing using nitrogen was adopted to perforate the stencil membrane. An acrylic well plate compartment mold was fabricated using computer numerical control (CNC) machining. By PDMS casting using a stencil placed on an acrylic mold, microwell plates were fabricated without punching or the use of a plasma bonding process. By using the stencil as a physical mask for the cell culture, PNs and NSCs were successfully cultured into micropatterns. The microwell plate could be applied to the localizing and culturing of a cell. The micropatterned NSCs were differentiated into neurons, astrocytes, and oligodendrocytes. The results showed that cells could be cultured and differentiated into micropatterns in a precisely controlled manner in any shape and in specific sizes for bioscience study and bioengineering applications.

We present a novel microvalve for the treatment of a pathological condition, i.e., hydrocephalus. This microvalve is made of polydimethylsiloxane/Parylene composite layer which has a 3-D dome petal shape. This geometry enables the microvalve to rectify fluid flow in the forward and backward directions. New microfabrication techniques such as dome-shaped SU-8 mold fabrication and excimer laser machining for valve opening have been investigated to build the proposed microvalve. The pressure drop versus flow rate characteristics of the fabricated microvalve was investigated through in vitro flow tests. The flow test results showed that a 10 × 10 microvalve array with a cross-cut opening shape (200 × 60 μm) was found to be optimal for the treatment of hydrocephalus.