Non-isocyanate polyurethanes (NIPUs) represent a sustainable alternative to conventional isocyanate-based systems, eliminating toxic reagents while maintaining good performance. In this study, bio-based NIPU coatings were synthesized from carbonated soybean oil (CSBO) via the carbonation of epoxidized soybean oil (ESBO) using carbon dioxide (CO₂), followed by polymerization with ethylenediamine (EDA) and varying concentrations of 3-aminopropyltriethoxysilane (APTES) (0–20 wt%). The amine groups of EDA and APTES participate in the ring-opening of cyclic carbonates to form β-hydroxyurethane linkages, while the triethoxysilane moieties of APTES may undergo hydrolysis–condensation to produce Si–O–Si domains, resulting in a β-hydroxyurethane–siloxane hybrid network. The optimized formulation CEA-5 exhibited the best, including a tensile strength of 3.3 MPa, elongation at break of ~150%, glass transition temperature (T_g) of ~7 °C, and thermal stability up to ~350 °C, where major thermal degradation happens. The synthesized coating material also shows adhesion (3.6 MPa on oak for CEA-10), hydrophobic behavior (water contact angle (WCA) ~102° for CEA-5), good chemical and ultraviolet (UV) resistance, and shape memory. The synergistic effect of urethane hydrogen bonding and siloxane crosslinking imparted enhanced toughness, flexibility, and durability. These findings express a scalable, eco-friendly strategy for producing silane-modified NIPU coatings with good mechanical, thermal, and coating performance suitable for sustainable industrial coating and adhesive applications.