Polyethylene (PE) films are widely used as waterproofing materials on the surfaces of metal pipelines. Poor adhesion of PE films to a metal substrate reduces durability, leading to shorter service life and higher economic costs. The current research aims to study the modification of PE films in atmospheric pressure gliding arc plasma (GAP). The adhesion properties of the modified films were investigated using the contact angle method and adhesion work calculations. During the modification process, the GAP treatment duration and deflector nozzle angle of attack were optimized to 10 s and 135°, respectively. It was established that the adhesion work increased from 62.1 to 141.3 mJ/m² after 10 s GAP modification compared to untreated PE. GAP modifying of PE films for 30 s or more is impractical, as the increase in the adhesion work ceases after that. It was found that surface roughness R_max increased by up to 4.1 times after 10 s GAP modification compared with nontreated PE. The PE films acquired hydrophilic properties after plasma modification, due to changes in the polymer surface’s chemical structure. The results of IR spectroscopy studies indicated oxidation of the film surface, an increase in the concentration of surface polar groups (-COOH, OH, C=O), and the formation of double bonds (C=C), which led to improved adhesive properties. A study of the electret properties showed that the observed decline and subsequent stabilization of values occurred within the first 24 h. Mechanical tests indicated improved performance of the GAP-modified PE films compared to the non-treated ones in the PE–mastic–PE and PE–mastic–steel systems. Due to their enhanced contact properties, the modified PE films are of interest as a base material for creating waterproofing materials.

ПЛАЗМЕННАЯ МОДИФИКАЦИЯ ПОВЕРХНОСТИ ПОЛИПРОПИЛЕНОВЫХ ПЛЕНОК ПРИ АТМОСФЕРНОМ ДАВЛЕНИИ