The 6xxx-series Al alloys have been used for decades because of their favorable strength-to-weight ratio, corrosion resistance, and fatigue performance. However, conventional welding techniques often induce localized weakening, as thermal effects modify the microstructure and compromise structural integrity. For nearly 70 years, AA4043 welding wire has been the primary choice for joining 6xxx-series Al alloys. Nevertheless, microstructural and mechanical property mismatches between the base metal and weld region remain key factors contributing to premature failure, while welding-induced defects further increase rupture susceptibility. Microalloying has emerged as an effective strategy for enhancing both the mechanical and thermal properties of aluminum alloys. In this study, rare-earth (RE) elements La and Ce were introduced into the AA4043 system to exploit their grain refining and mechanical strengthening capabilities. In addition, the effects of Sr modification were examined and compared with La-Ce addition. This work aims to elucidate the strengthening mechanisms associated with La-Ce-Ti microalloying in AA4043 welding wire, a topic that has rarely been systematically investigated. With 0.019Ti-0.02La-0.03Ce additions, the modified wire exhibited significant performance improvements, achieving an UTS of 204 MPa and a YS of 191 MPa—representing increases of 10.3% and 18.6%, respectively.