Creation of hydrophobic and superhydrophobic surfaces has attracted broad attention as a promising solution for protection of metal surfaces from corrosive environments. This work investigates the capability of nanosecond fiber laser surface texturing followed by a low energy coating in the fabrication of hydrophobic 17-4 PH stainless steel surfaces as an alternative to the ultrashort lasers previously utilized for hydrophobic surfaces production. Laser texturing of the surface followed by applying the hydrophobic coating resulted in steady-state contact angles of up to 145°, while the non-textured coated base metal exhibited the contact angle of 121°. The microstructure and compositional analysis results confirmed that the laser texturing process neither affects the microstructure of the base metal nor causes elemental loss from the melted regions during the ultrafast melting process. However, the electrochemical measurements demonstrated that the water-repelling property of the surface did not contribute to the anticorrosion capability of the substrate. The resultant higher corrosion current density, lower corrosion potential, and higher corrosion rate of the laser textured surfaces were ascribed to the size of fabricated surface micro-grooves, which cannot retain the entrapped air inside the hierarchical structure when fully immersed in a corrosive medium, thus degrading the material’s corrosion performance.

In this study, the effects of microstructural modifications induced by tuning the laser-powder bed fusion (L-PBD) process parameters on electrochemical stability of the L-PBF-AlSi10Mg alloy are investigated. Three groups of L-PBF-AlSi10Mg samples were fabricated utilizing combinations of L-PBF process parameters for their Upskin layers. The implemented process parameters modifications were found to be not only effective in reducing the as-printed surface roughness of the components, but also led to the formation of cyclic small-large melt pools (MPs) in Upskin layers of the fabricated samples. Such consecutive modification in the size of MPs led to the increased inhomogeneity of the microstructure, contributing to the formation of a coarser intercellular eutectic-Si network, larger grain size, and lower density of low angle grain boundaries. Among all fabricated samples, the sample that experienced the fastest cooling during solidification was found to reveal the highest corrosion resistance and the best passive film stability on its Upskin surface both in naturally-aerated and deaerated 3.5 wt.% NaCl electrolyte, owing to the finer Al-Si eutectic structure that forms along its large MP-boundaries. The as-printed microstructure of the L-PBF-AlSi10Mg was found a dominant factor in determining the necessity of applying post-printing surface polishing procedures to attain better corrosion properties.