Two series of segmented polyurethanes were obtained and their mechanical and thermal properties as well as their biodegradability and cytotoxicity were evaluated. The chemical nature of the polyurethanes was varied by using either 1,4 butanediol (poly-ester-urethanes, PEUs) or l-lysine ethyl ester dihydrochloride (poly-ester-urea-urethanes, PEUUs) as chain extenders. Results showed that varying the hard segment influenced the thermal and mechanical properties of the obtained polymers. PEUs showed strain and hardness values of about 10–20 MPa and 10–65 MPa, respectively. These values were higher than the obtained values for the PEUUs due to the phase segregation and the higher crystallinity observed for the polyester-urethanes (PEUs); phase segregation was also observed and analyzed by XRD and DSC. Moreover, both series of polymers showed hydrolytic degradation when they were submerged in PBS until 90 days with 20% of weight loss. In vitro tests using a Human Osteoblastic cell line (Hob) showed an average of 80% of cell viability and good adhesion for both series of polymers.

A series of non-toxic biodegradable and biocompatible polyurethanes bearing p-aminobenzoate moieties are presented. The introduction of this attractive motif was carried out by the synthesis of a novel isocyanate. These biodegradable polymers were chemically and physically characterized by several techniques and methods including bioassay and water uptake measurements. The molecular weight of the soft segment (poly-ε-caprolactone, PCL) and hard segment crystallinity dictated the mechanical behavior and water uptake. The behavior of short PCL-based polyurethanes was elastomeric, whilst increasing the molecular weight of the soft segment led to plastic polyurethanes. Water uptake was hindered for long PCL due to the crystallization of the soft segment within the polyurethane matrix. Furthermore, two different types of chain extender, hydrolyzable and non-hydrolyzable, were also evaluated: polyurethanes based on hydrolyzable chain extenders reached higher molecular weights, thus leading to a better performance than their unhydrolyzable counterparts. The good cell adhesion and cytotoxicity results demonstrated the cell viability of human osteoblasts on the surfaces of these non-toxic biodegradable polyurethanes.

The influence of L-lactide content (between 15% and 43%) on the degradation of biodegradable polyurethanes (PUs) for tissue engineering was systematically addressed in this study. An ideal tissue scaffold should exhibit a mechanical response and degradability appropriate for the host tissue. To achieve it, polyols containing ε-caprolactone and L-lactide moieties were used, with the random distribution of lactide units disrupting the regularity, and hence the crystallinity, of poly(caprolactone) segments, facilitating their degradation. The biodegradable PUs were synthesised using these copolymers as soft segments and were characterised through various physicochemical techniques, including bioassays and water absorption measurements. It was determined that mechanical behaviour and water absorption depended significantly on molecular weight, L-lactide content in the soft segment, and the crystallinity of the hard segment. Additionally, two types of chain extenders were also evaluated: hydrolysable and non-hydrolysable. PUs based on hydrolysable chain extenders achieved higher molecular weights and exhibited better mechanical performance than their non-hydrolysable counterparts. To assess the cytocompatibility of these materials, an endothelial model was used, involving metabolic activity and DNA content analysis. The results demonstrated good cell adhesion and the absence of toxicity, confirming the viability of cell growth on the surfaces of these biodegradable PUs. The PUs developed in this study exhibited a low initial modulus and adjustable mechanical properties, highlighting their potential application in tissue engineering as biodegradable and biocompatible biomedical materials.

Hybrid materials have been studied because in these materials the properties of organic components, such as elasticity and biodegradability, could be combined with the properties of inorganic components, such as good biological response, thereby transforming them into a single material with improved properties. In this work, Class I hybrid materials based on polyester-urea-urethanes and titania were obtained using the modified sol–gel method. This was corroborated using the FT-IR and Raman techniques which highlighted the formation of hydrogen bonds and the presence of Ti–OH groups in the hybrid materials. In addition, the mechanical and thermal properties and degradability were measured using techniques, such as Vickers hardness, TGA, DSC, and hydrolytic degradation; these properties could be tailored according to hybridization between both organic and inorganic components. The results show that Vickers hardness increased by 20% in hybrid materials as compared to polymers; also, the surface hydrophilicity increases in the hybrid materials, improving their cell viability. Furthermore, cytotoxicity in vitro test was carried out using osteoblast cells for intended biomedical applications and they showed non-cytotoxic behavior.