Cobalt nanoparticles were synthesized using the gamma radiolytic technique, and the particle size was found to be reduced from $12\pm 1$ to $7\pm 1$ nm by increasing the dose from 10 to 60 kGy. The UV-visible absorption spectra were measured and exhibited a steady absorption maxima at 517 nm in the UV region, which blue-shifted toward a lower wavelength with a decrease in particle size. By taking the conduction electrons of an isolated particle that are not entirely free but are instead bound to their respective quantum levels, the optical absorption of the cobalt nanoparticles can be calculated and simulated via intra-band quantum excitation for particle sizes comparable to the measured ones. We found that the simulated absorption maxima of electronic excitations corresponded to the measured absorption maxima. Moreover, the structural characterizations were performed utilizing dynamic light scattering (DLS), transmission electron microscopy (TEM), and X-ray diffraction (XRD).

The purpose of this research is to examine how the electro-optical behavior of platinum (Pt) nanoparticles prepared via the gamma radiolysis process is related to both the radiation dose and to the Pt precursor concentration. The Pt precursor used in these experiments has been radiolytically degraded using a ⁶⁰Co gamma source at dosages ranging from 80 kGy to 120 kGy. As well, varying the concentration of the Pt precursor from 5.0 × 10⁻⁴ M to 20.0 × 10⁻⁴ M was carried out as a systematic investigation. Spectrophotometric analysis utilizing UV–Visible spectroscopy and TEM provided the optical data and particle size information for the nanoparticles. The results indicate that increasing the radiation dosage results in smaller Pt nanoparticle sizes due to an increased rate of nucleation and that increasing the Pt precursor concentration leads to larger Pt nanoparticles due to an increase in ion recombination. Both the dose and concentration dependency of the optical absorption spectrum indicate a significant relationship between size and plasmon behavior. Also, the conduction band energy level, which was determined from the maximum of the UV–Visible absorption peak, is dependent on the particle size and shows a pronounced quantum confinement effect, with the conduction band energy increasing as the particle size decreases. Thus, these studies provide a definitive correlation of structure–property in Pt nanoparticles and confirm the capability of the gamma radiolytic synthesis process to be used for controlling the specific electronic and optical properties of Pt nanoparticles.