In this study, we simulated the electric field distribution of side-by-side electrospinning by using the finite element method (FEM), and studied the effects of spinneret wall thickness, spinning voltage and receiving distance on the distribution of the electrostatic field. The receiving distance was selected as a variable in the experimental, a series of PAN/PSA composite nanofiber membranes were prepared by using a self-made side by side electrospinning device. The membranes were tested by Fourier-transform infrared (FTIR), thermogravimetric analysis (TG), and scanning electron microscope (SEM). The prepared membranes were also treated by high-temperature treatment, and the change of fiber diameter and conductivity of the membrane before and after high-temperature treatment were studied. It was found that the PAN/PSA carbonized nanofibers could achieve a better performance in heat resistance and conductivity at 200 mm receiving distance.

Structural-coloured poly(styrene-methyl methacrylate-acrylic acid) (Poly(St-MMA-AA)) deposited carbon fabrics (Poly(St-MMA-AA)/PCFs) with fascinating colours (salmon, chartreuse, springgreen, skyblue, mediumpurple) changing with the (Poly(St-MMA-AA) nanoparticle sizes can be facilely fabricated by the thermal-assisted gravity sedimentation method that facilitates the self-assembly of Poly(St-MMA-AA) colloidal nanoparticles to generate photonic crystals. The particle sizes of Poly(St-MMA-AA) copolymer with core/shell structure varying from 308.3 nm to 213.1 nm were controlled by adjusting the amount of emulsifier during emulsion polymerisation. The presence of the intrinsic chemical information of Poly(St-MMA-AA) copolymer has been ascertained by Raman and Fourier Transform Infrared (FT-IR) Spectroscopy analysis. Colour variation of the as-prepared structural-coloured carbon fabrics (Poly(St-MMA-AA)/PCFs) before and after dipping treatment were captured while using an optical microscope. The structural colours of Poly(St-MMA-AA)/PCFs were assessed by calculating the diffraction bandgap according to Bragg’s and Snell’s laws. The Poly(St-MMA-AA) photonic crystal films altered the electrical properties of carbon fabrics with the resistivity growing by five orders of magnitude. The differential electrical resistivity between Poly(St-MMA-AA)/PCFs and wet Poly(St-MMA-AA)/PCFs combined with the corresponding tunable colours can be potentially applied in several promising areas, such as smart displays, especially signal warning displays for traffic safety.

Structural color derived from the physical interactions of photons, with the specific chromatic mechanism differing from that of dyes and pigments, has brought considerable attention by the conducive virtue of being dye-free and fadeless. This has recently become a research hot-spot. Assemblies of colloidal nanoparticles enable the manufacture of periodic photonic nanostructures. In our review, the mechanism of nanoparticle assemblies into structurally colored structures by the electrospinning method was briefly introduced, followed by a comparatively comprehensive review summarizing the research related to photonic crystals with periodically aligned nanostructures constructed by the assembly of colloidal nanoparticles, and the concrete studies concerning the fabrication of well-aligned electrospun nanofibers incorporating with colloidal nanoparticles based on the investigation of relevant factors such as the sizes of colloidal nanoparticles, the weight ratio between colloidal nanoparticles, and the polymer matrix. Electrospinning is expected to be a deserving technique for the fabrication of structurally colored nanofibers while the colloidal nanoparticles can be well confined into aligned arrangement inside nanofibres during the electrospinning process after the achievement of resolving remaining challenges.

This study investigates the feasibility of using biodegradable secondary alcohol ethoxylate (SAE) non-ionic surfactant as a building block for the formation of reverse micelles, functioning as reactive dye carriers for the dyeing of cotton fabric in non-aqueous octane medium. Ten dyeing parameters were optimised, by a one-factor-at-a-time approach, namely: (i) effect of colour fixation agent; (ii) surfactant-to-water mole ratio; (iii) surfactant-to-co-surfactant mole ratio; (iv) volume of soda ash; (v) volume of dye; (vi) solvent-to-cotton ratio; (vii) dyeing temperature; (viii) dyeing time; (ix) fixation time; (x) soda-ash-to-cotton ratio. The colour properties, fastness properties and physical properties of SAE-dyed samples were experimentally compared with the conventional water-dyed samples. The optimised condition was found when SAE samples were dyed as follows: (a) 1:20 surfactant-to-water ratio; (b) 1:8 surfactant-to-co-surfactant ratio; (c) 10:1 solvent ratio; (d) 40 min dyeing time; (e) 60 min fixation time; and (f) 70 °C dyeing and fixation temperature. The results showed that SAE-dyed samples have better colour strength, lower reflectance percentage and comparable levelness, fastness and physical properties than that of water-dyed samples. SEM images revealed that the dyed cotton fibres had no severe surface damage caused by an SAE-based reverse micellar dyeing system. The TEM image depicts that the reverse micelle was of nanoscale, spherical-shaped and had a core–shell structure, validating the presence of reverse micelle as a reactive dye carrier and the potential of an SAE-based reverse micellar system for dyeing of cotton fabrics.

In this study, the inclusion of graphene oxide in silica photonic crystals was found to affect optical reflectance intensity and reflectance peak broadening. The quantitative relationship between weight percentage and the reflected light intensity and corresponding wavelength shift of light GO-decorated photonic crystals was studied, providing a useful parameter in the rational design of antireflection coatings for GO-based photonic crystal films. Comparison of the experimental results with a pure SiO₂ particle film shows that a SiO₂ particle surface layer incorporated with a fixed graphene oxide weight percentage results in broadening of the peak and a decrease in reflectance intensity. The percentage of the reduction in reflectance intensity is a function of particle size, as indicated by the structured color film surface, demonstrating the possibility of estimating the effect of different graphene oxide inclusion percentages on the antireflection properties of photonic crystal films.