The balance of carbon dioxide emissions and other greenhouse gases in the life cycle of concrete is one of the important elements affecting the sustainable development of concrete technology. Modifications in the composition in the aim of minimization of so-called “carbon footprint” of concrete also affect the majority of its technical features, including primarily the mechanical properties and durability. The article presents a desirability function that would allow us to estimate the combined effect of the modification in terms of both CO₂ emissions and some of the technical features of the concrete. As criterial features equivalent CO₂ emission, compressive strength and susceptibility/resistance to concrete carbonation are selected. Selected features should be considered as an example for the presentation of the proposed methodology and represent the three pillars of concrete desirability in terms of sustainable development, i.e., the constructional usefulness, durability, and environmental performance.

Cemented stabilized rammed earth (CSRE) is a building material used to build load bearing walls from locally available soil. The article analyzes the influence of soil mineral composition on CSRE compressive strength. Compression tests of CSRE samples of various mineral compositions, but the same particle size distribution, water content, and cement content were conducted. Based on the compression strength results and analyzed SEM images, it was observed that even small changes in the mineral composition significantly affected the CSRE compressive strength. From the comparison of CSRE compressive strength result sets, one can draw general qualitative conclusions that montmorillonite lowered the compressive strength the most; beidellite also lowered it, but to a lesser extent. Kaolinite lightly increased the compressive strength.

One of the main threats to constructions made from rammed earth is destruction due to exposure to water. The way to limit this dangerous phenomenon is to supplement the local soil mixtures with stabilizing agents. The main component used is Portland cement. This article analyses the results of research which focused on the resistance of rammed earth to water erosion. Because of the lack of national standards regarding the method of examining the durability of rammed earth, the research was based on the New Zealand standard NZS 4298: 1998. The results confirm the possibility of using rammed earth stabilized by cement in a temperate climate.

This paper examines the influence of dosing method and material characteristic of superabsorbent polymers (SAP) used for internal curing, on the selected concrete properties. A new method of introducing SAP into the concrete mix and its impact on the shrinkage and compressive strength of concrete was studied. It was shown that the method of dosing SAP to the concrete mix and the differences in the properties of the tested SAPs have a significant impact on the course of changes of selected properties of the tested concrete composites. In order to compare tested series with each other and with other published results on the subject, a new method of including SAP mass content in the concrete mix, as a percentage of absorbed mixing water, was presented. The effectiveness of internal curing using different types of SAP under different dosing methods was presented as a percentage difference in tested concrete properties between modified series and reference series.

The article compared the test results of a number of features determining the durability of rammed earth durability in a humid continental climate. The results of wet to dry compressive strength ratio, frost resistance, linear shrinkage, resistance to erosion under the influence of a stream of pressurized water, and resistance to erosion under the influence of cyclic wetting and drying were presented. All of the tests were done on the same soil-cement mixture. On this basis, it was determined which of the methods of durability assessment is more and which is less restrictive. A new method for assessing the durability of CSRE in a humid continental climate has been proposed, which is the frost resistance test. This test is determined by the method that is described in the national annex of the European concrete standard of one of the temperate climate countries. The article also shows that a minimum of 9% of the cement additive and a soil mixture containing a gravel fraction are required, in order to ensure adequate rammed earth durability in a humid continental climate (i.e., frost resistance).