In this study, manganese ferrite was grown on the surface of a low-cost powder substrate of a guava leaf using the co-precipitation method. The resulting material was characterized using various spectroscopic and microscopic techniques. The composite was formed through the electrostatic and non-electrostatic interactions between the manganese ferrite nanoparticles, and the functional groups present on the guava leaf substrate; consequently, a high content of functional groups was observed in the synthesized composite through the Fourier transform infrared spectroscopy. The average size of the nanoparticles grown on the guava leaf substrate was determined to be between 3 and 5 nanometers. The synthesized composite material was utilized for adsorption applications, employing Methylene blue dye as a model adsorbate. Methylene blue was removed from the aqueous solutions under various conditions—including variations in the pH, contact time, temperature, and concentration. Under optimal conditions, it was observed that an adsorbent dosage of 2 g L⁻¹ was capable of removing approximately 99% of the dye from a 10 mg L⁻¹ dye solution at pH 7. The dye removal efficiency (%) decreased with the increasing temperature, indicating an exothermic process; this was further confirmed by the thermodynamic parameter analysis (specifically, the change in enthalpy, or ΔH), which yielded a negative value. Gibbs Free Energy (ΔG) also yielded a negative value, signifying the feasibility and spontaneity of the adsorption process. In this study, the adsorption process followed the Freundlich isotherm model, with the value of ‘n’ falling between 1 and 10, which is indicative of heterogeneous adsorption. The adsorption kinetics were determined to follow a pseudo-second-order model, and the overall rate-limiting step of the process was identified as intraparticle diffusion. To assess the sustainability and stability of the adsorbent, regeneration and reusability experiments were conducted. The results revealed that the modified guava leaf performed effectively for up to five cycles, achieving an adsorption efficiency of approximately 24% after the final cycle. Thus, the developed adsorbent proved to be an effective material for the removal of Methylene blue dye.

This study reports the preparation of a nanocomposite using a black cumin surface as a carbon framework on which zinc oxide-doped manganese ferrite nanoparticles were deposited and grown. A simple precipitation method was used to prepare the nanocomposite. The resulting composite was characterized using various characterization analyses such as FTIR, XRD, EDX, SEM, TEM, and TGA. The composite surface was highly conformed with functional groups, and the nanocomposite was formed due to electrostatic and non-electrostatic interactions between the carbon framework and the nanoparticles. X-ray analysis revealed a crystalline structure with crystal sizes up to 45 nm. Microscopic images revealed the surface morphology, confirming the irregular distribution of particles within the composite. The resulting composite material was used for adsorption application. The composite material was tested for the removal of Congo red dye from water. It was found that under optimal conditions, a dose of 2 g per liter of absorbent removed nearly 100% of dye from a 10 mL volume of 10 mg per liter Congo red solution within 90 min and 7 pH. A monolayer adsorption was confirmed by the isotherm analysis. The monolayer adsorption capacity for the present study was ~13.0 mg per gram. The adsorption kinetics suggested the fitting of pseudo-second order. Based on the findings, it was concluded that the chemical mechanism was responsible for the present adsorption process. The regeneration study demonstrates the stability of current adsorbent up to two cycles only. This nanocomposite is the first of its kind which promotes the creation of nanocomposites in the future by using natural materials and reduces the dependency on activated carbon.