The structure of dispersions of TEMPO-oxidised cellulose nanofibrils (OCNF), at various concentrations, in water and in NaCl aqueous solutions, was probed using small angle X-ray scattering (SAXS). OCNF are modelled as rod-like particles with an elliptical cross-section of 10 nm and a length greater than 100 nm. As OCNF concentration increases above 1.5 wt%, repulsive interactions between fibrils are evidenced, modelled by the interaction parameter ν_RPA > 0. This corresponds to gel-like behaviour, where G′ > G′′ and the storage modulus, G′, shows weak frequency dependence. Hydrogels can also be formed at OCNF concentration of 1 wt% in 0.1 M NaCl(aq). SAXS patterns shows an increase of the intensity at low angle that is modelled by attractive interactions (ν_RPA < 0) between OCNF, arising from the screening of the surface charge of the fibrils. Results are supported by ζ potential and cryo-TEM measurements.

A novel mechanism of heat-triggered gelation for oxidised cellulose nanofibrils (OCNF) is reported. We demonstrate that a synergistic approach combining rheology, small-angle X-ray scattering (SAXS) and saturation transfer difference NMR (STD NMR) experiments enables a detailed characterisation of gelation at different length scales. OCNF dispersions experience an increase in solid-like behaviour upon heating as evidenced by rheological studies, associated with enhanced interfibrillar interactions measured using SAXS. Interactions result in an increased fibrillar overlap and increased population of confined water molecules monitored by STD NMR. In comparison, cationic cellulose nanofibrils (produced by reaction of cellulose with trimethylglycidylammonium chloride) were found to be heat-unresponsive.

Through the use of low voltage high resolution scanning electron microscopy (LV-HRSEM) we have studied the fine details of the intricate pore structure of SBA-15. Intrawall pores and deviations from the ideal and uniform cylindrical pores are clearly observed, and we report for the first time the direct observation of “plugs” in the pores. N₂-sorption measurements confirm their existence. LV-HRSEM provides an opportunity to quantify the frequency of occurrence of plugs within the pore structure. The rate of mesophase formation, followed with in situ small angle X-ray scattering (SAXS) under different solvent conditions, is shown to have a significant influence on the development of plugs and how frequently they occur. We suggest a mechanism explaining the existence of the plugs, providing means for a better understanding and control over material properties.