This paper reports the electrochemical, optical and thermal effects occurring during flash sintering of 8 mol % yttria-stabilized zirconia (8YSZ). In-situ observations of polycrystalline and single crystal specimens revealed electrochemical blackening/darkening during an incubation period prior to flash sintering. The phenomenon is induced by cathodic partial reduction under DC fields. When using a low frequency AC field (0.1–10 Hz) the blackening is reversible, following the imposed polarity switching. Thermal imaging combined with sample colour changes and electrical conductivity mapping give a complete picture of the multi-physical phenomena occurring during each stage of the flash sintering event. The partial reduction at the cathode causes a modification of the electrical properties in the sample and the blackened regions, which are close to the cathode, are more conductive than the remainder of the sample. The asymmetrical nature of the electrochemical reactions follows the field polarity and causes an asymmetry in the temperature between the anode and cathode, with the positive electrode tending to overheat. It is also observed that the phenomena are influenced by the quality of the electrical contacts and by the atmosphere used.

A processing approach has been identified and reduced to practice in which a residual stress profile can be designed such that cracks in a brittle material are arrested or grow in a stable manner. In the approach, cracks in the body encounter an increase in the magnitude of residual compression as the crack propagates. If correctly designed, the process increases strength and significantly decreases strength variability. This approach was demonstrated for a silicate glass, and multiple cracking was observed as a forewarning of the final failure. Normally, such glasses would fail catastrophically with the propagation of a dominant crack.