Bio-based phytic acid (PA) as a nontoxic naturally occurring compound is a promising prospect for flame-retardant (FR) modifications to polymers. In this work, PA was applied to wool fabric using an exhaustion technique, and the adsorption and FR properties of PA on wool fabric were studied. The flame retardancy of the treated wool fabrics depended greatly on the adsorption quantity of PA, which was related to the pH of treatment solution, immersing temperature and initial PA concentration. The Langmuir adsorption of PA took place due to electrostatic interactions between PA and wool fiber. The limiting oxygen index, vertical burning and pyrolysis combustion flow calorimetry tests revealed that the treated wool fabrics exhibited good flame retardancy. The measurements of the phosphorus content of the burned fabric residues and thermogravimetric analyses suggested that a significant condensed-phase FR action was applicable to the PA treated fabrics. PA treatment was found to have little adverse effect on the whiteness and mechanical performance of wool. Additionally, the washing resistance of the FR fabrics should be further improved.

Keratin from a variety of sources is one of the most abundant biopolymers. In livestock and textile industries, a large amount of rabbit hair waste is produced every year, and therefore it is of great significance to extract keratin from waste rabbit hair in terms of the treatment and utilization of wastes. In this study, a novel, eco-friendly and benign choline chloride/oxalic acid deep eutectic solvent at a molar ratio of 1:2 was applied to dissolve waste rabbit hair, and after dissolution keratin was separated by dialysis, filtration, and freeze-drying. The dissolution temperature effect was discussed, and the resulting keratin powder was characterized by X-ray diffraction, scanning electron microscope, Fourier transform infrared spectroscopy, protein electrophoresis, thermogravimetry and differential scanning calorimetry, and amino acid analysis. During the dissolution process, the α-helix structure of rabbit hair was deconstructed, and the disulfide bond linkages were broken. The solubility of rabbit hair was significantly enhanced by increasing dissolution temperature, and reached 88% at 120 °C. The keratin produced by dissolving at 120 °C displayed flaky powders after freeze-drying, and had a molecular weight ranging from 3.8 to 5.8 kDa with a high proportion of serine, glutamic acid, cysteine, leucine, and arginine. Such features of molecular weight and amino acid distribution provide more choices for the diverse applications of keratin materials.

Wool keratin/poly(vinyl alcohol) (PVA) blend nanofibers were fabricated using the electrospinning method in formic acid solutions with different weight ratios of keratin to PVA. The resultant blend nanofibers were characterized by scanning electron microscopy (SEM), Fourier transform infrared (FTIR), X-ray diffraction (XRD), thermal gravimetric analysis (TGA), and tensile test. SEM images showed that the diameter of the blend nanofibers was affected by the content of keratin in blend solution. FTIR and XRD analyses data demonstrated that there were good interactions between keratin and PVA in the blended nanofibers caused by possibly hydrogen bonds. The TGA study revealed that the thermal stability of the blend nanofibers was between those of keratin and PVA. Tensile test indicated that the addition of PVA was able to improve the mechanical properties of the electrospun nanofibers.

Rapid wound dressings provide an excellent solution strategy for the treatment of wounds in emergency situations. In this study, aqueous solvent-based PVA/SF/SA/GelMA nanofiber dressings fabricated by a handheld electrospinning device could deposit quickly and directly on the wound, perfectly fitting wounds with various sizes. Using an aqueous solvent overcame the disadvantage of using the current organic solvents as the medium for rapid wound dressings. The porous dressings had excellent air permeability to ensure smooth gas exchange at the wound site. The distribution range of the tensile strength of the dressings was 9–12 Kpa, and the tensile strain was between 60–80%, providing sufficient mechanical support during wound healing. The dressings could absorb 4–8 times their own weight in solution and could rapidly absorb wound exudates from wet wounds. The nanofibers formed ionic crosslinked hydrogel after absorbing exudates, maintaining the moist condition. It formed a hydrogel–nanofiber composite structure with un-gelled nanofibers and combined the photocrosslinking network to maintain a stable structure at the wound location. The in vitro cell culture assay indicated that the dressings had excellent cell cytocompatibility, and the addition of SF contributed to cell proliferation and wound healing. The in situ deposited nanofiber dressings had excellent potential in the urgent treatment of emergency wounds.