The potential of ultrasonic surface mechanical attrition treatment (SMAT) at different temperatures (including cryogenic) for improving the fatigue performance of 304L austenitic stainless steel is evaluated along with the effect of the fatigue loading conditions. Processing parameters such as the vibration amplitude, the size, and the material of the shot medias were fixed. Treatments of 20 min at room temperature and cryogenic temperature were compared to the untreated material by performing rotating–bending fatigue tests at 10 Hz. The fatigue limit was increased by approximately 30% for both peening temperatures. Meanwhile, samples treated for 60 min at room temperature were compared to the initial state in uniaxial fatigue tests performed at R = −1 (fully reversed tension–compression) at 10 Hz, and the fatigue limit enhancement was approximately 20%. In addition, the temperature measurements done during the tests revealed a negligible self-heating (∆t < 50 °C) of the run-out specimens, whereas, at high stress amplitudes, temperature changes as high as 300 °C were measured. SMAT was able to increase the stress range for which no significant local self-heating was reported on the surface.

Ultrafine-grained Al matrix nanocomposites, reinforced with Al₂O₃ nanoparticles, were produced from milled powders, either by equal channel angular pressing (ECAP), at room or high temperature, with or without back pressure, or by spark plasma sintering (SPS). Their microstructures, mechanical properties (compression, hardness, and sliding wear), and thermal stabilities (thermally induced softening and cracking) were compared, and the advantages and limitations of each process discussed on a scientific but also practical point of view. For the most successful set of process parameters, the yield stress in compression reached 380 MPa, the hardness, HV = 139, remained stable up to 500 °C, and the resistance to sliding wear was comparable to that of Al 5083, and better than that of Al 7075-T6. While the samples consolidated at high temperatures (by ECAP or SPS) showed a good thermal stability, those consolidated by ECAP at room temperature were prone to thermally induced softening and cracking, which was related to trapped and pressurized gases.