The aim of this study was to evaluate the effects of γ-irradiation (IR), ultrasound (US), and combined treatments of ultrasound followed by γ-irradiation (US-IR), ultrasound followed by enzymatic hydrolysis with and without centrifugation (US-E and US-EWC, respectively), and ultrasound followed by γ-irradiation and enzymatic hydrolysis (US-IRE), on the digestibility and the nutritional value of fermented beverages containing probiotics. Results showed that US (20 min), IR (3 kGy) and US-IR (t_US = 20 min, dose = 3 kGy) treatments raised protein solubility from 11.5 to 21.5, 24.3 and 29.9%, respectively. According to our results, these treatments were accompanied by the increased amount of total sulfhydryl groups, surface hydrophobicity and changes to the secondary structure of the proteins measured by Fourier-transform infrared spectroscopy (FTIR). Fermented probiotic beverages, non-enriched (C) and enriched with untreated (Cr) or treated cricket protein with combined treatments were also evaluated for their in vitro protein digestibility. Results showed that the soluble fraction of US-IRE fermented beverage had the highest digestibility (94%) as compared to the whole fermented tested beverages. The peptides profile demonstrated that US-IRE had a low proportion of high molecular weight (M_W) peptides (0.7%) and the highest proportion of low M_W peptides by over 80% as compared to the other treatments.

This study explores a new eco-friendly approach for developing bioactive gelatin films using UV-C irradiation-induced photo-crosslinking. Riboflavin, a food-grade photoinitiator, was selected at an optimal concentration of 1.25% (w/w) for crosslinking gelatin under UV-C exposure for 4 to 22 min. Physicochemical analyses revealed enhanced tensile strength, reduced water vapor permeability, and lower water solubility in films crosslinked for up to 13 min. FTIR analysis demonstrated significant molecular changes, confirming the formation of crosslinking connections in gelatin–riboflavin films. Antimicrobial nanoemulsion (NE) (0.5, 0.75, 1% v/v) was incorporated into crosslinked films and applied to fresh beef. The 1% NE film exhibited the strongest antimicrobial effect, extending shelf-life by 20 days. In vitro release study confirmed Fickian diffusion behavior in the 1% NE film. This study also investigated the synergy between 1% NE film and three different types of modified atmosphere packaging (MAP) on the microbiological and physicochemical properties of beef for 26 days. The best results were achieved with 1% NE film under MAP1 and MAP2, which preserved meat redness and prevented lipid oxidation, extending the shelf-life up to 26 days. Therefore, UV-C irradiation-induced crosslinked bioactive film combined with high-oxygen MAP offers a promising solution for prolonging the shelf-life of beef.

The health and balance of the gut microbiota are known to be linked to diet composition and source, with fermented products and dietary proteins potentially providing an exceptional advantage for the gut. The purpose of this study was to evaluate the effect of protein hydrolysis, using a probiotic beverage enriched with either cricket protein (CP) or cricket protein hydrolysates (CP.Hs), on the composition of the gut microbiota of rats. Taxonomic characterization of the gut microbiota in fecal samples was carried out after a 14-day nutritional study to identify modifications induced by a CP- and CP.H-enriched fermented probiotic product. The results showed no significant differences (p > 0.05) in the diversity and richness of the gut microbiota among the groups fed with casein (positive control), CP-enriched, and fermented CP.H-enriched probiotic beverages; however, the overall composition of the microbiota was altered, with significant modifications in the relative abundance of several bacterial families and genera. In addition, fermented CP.H-enriched probiotic beverages could be related to the decrease in the number of potential pathogens such as Enterococcaceae. The association of gut microbiota with the nutritional parameters was determined and the results showed that digestibility and the protein efficiency ratio (PER) were highly associated with the abundance of several taxa.

This study developed biodegradable carboxymethyl cellulose (CMC) films crosslinked with citric acid (CA) and X-ray irradiation as sustainable packaging alternatives to reduce plastic use. CMC/CA films were subjected to three doses of X-ray irradiation at two energy levels. CMC/CA films exposed to 10 kGy at 350 kV exhibited a significant three-fold reduction in water solubility compared to non-irradiated films, while also lowering water vapor and oxygen permeability without affecting mechanical strength (p ≤ 0.05). FTIR analysis confirmed the esterification between CMC and CA, which reduced the film hydrophilicity. Onion peel extract (OPE) was added as a bioactive compound to provide antifungal properties. Release studies showed reduced OPE diffusion in irradiated films, with lower release rate constant (k_kp) values. The in situ test on cheese inoculated with Penicillium commune showed that the irradiated bioactive films prolonged shelf life, reducing fungal counts to log 2.3 CFU/g after 18 days compared to log 5.7 CFU/g in control samples. Cheese wrapped with irradiated bioactive films had weight loss from 1.05 to 9.37%, whereas uncovered samples exhibited the highest weight loss (2.07 to 15.07%). Overall, irradiation-assisted crosslinking and OPE incorporation improved film functionality, offering a sustainable and effective packaging solution for cheese preservation within a circular economy framework.

Strawberry is a nutritive fruit with a short life and postharvest losses. In this study, the quality and shelf life of strawberries during storage at 4 °C were evaluated after applying hurdle treatment of packaging with active polylactic acid (PLA)/Gelatine (G)-based films loaded with essential oils (EOs) and/or AgNPs and combined with low-energy (L-E) X-ray at a dose of 0.5 kGy. The results showed that the addition of EOs, AgNPs, or their combination decreased the tensile strength (TS) of films from 16.70 to 6.65–10.01 MPa and increased elongation at break (Eb) from 215.4 to 218.2–398.2%. The oxygen transmission rate (OTR) of films increased from 219.7 to 274.8–298.6 cm³/m²·day, which promoted the development of gas selective films for equilibrium-modified atmosphere packaging (EMAP). A level of 20% decay (primary shelf life criterion) of strawberries was observed on day 8 for the commercial control (polyethylene terephtalate clamshell), on day 9 for the PLA/G-AgNPs films, and on day 10 for the PLA/G-EOs films and PLA/G-EOs + AgNPs films. The combined application of the active films with L-E X-ray irradiation (PLA/G/EOs + AgNPs + I) extended the time to reach 20% decay to day 13 compared to day 9 for irradiated commercial control. An EMAP was achieved after 6–9 days of storage, with a gas composition around 13–14% O₂ and 8–9% CO₂. The combined treatment of EOs, AgNPs containing films, and L-E X-ray irradiation prevented firmness and total soluble solid loss of strawberries. The redness of strawberries and their total phenolic/anthocyanin content increased after irradiation treatment and maintained significantly higher levels (p ≤ 0.05) than those of non-irradiated samples during storage. This study demonstrates the effectiveness of combining active PLA/G films and L-E X-ray irradiation in extending the shelf life and preserving the quality of fresh strawberries.