Current-carrying friction affects electrical contact systems like switches, motors, and slip rings, which determines their performance and lifespan. Researchers have found that current-carrying friction is influenced by various factors, including material type, contact form, and operating environment. This article first reviews commonly used materials, such as graphite, copper, silver, gold, and their composites. Then different contact forms like reciprocating, rotational, sliding, rolling, vibration, and their composite contact form are also summarized. Finally, their environmental conditions are also analyzed, such as air, vacuum, and humidity, on frictional force and contact resistance. Additionally, through experimental testing and theoretical analysis, it is found that factors such as arcing, thermal effects, material properties, contact pressure, and lubrication significantly influence current-carrying friction. The key mechanisms of current-carrying friction are revealed under different current conditions, including no current, low current, and high current, thereby highlighting the roles of frictional force, material migration, and electroerosion. The findings suggest that material selection, surface treatment, and lubrication techniques are effective in enhancing current-carrying friction performance. Future research should focus on developing new materials, intelligent lubrication systems, stronger adaptability in extreme environments, and low friction at the microscale. Moreover, exploring stability and durability in extreme environments and further refining theoretical models are essential to providing a scientific basis for designing efficient and long-lasting current-carrying friction systems.

Oxidation is a critical factor contributing to material wear and the degradation of conductive performance during current-carrying tribological processes. The present study investigated the composite oxidation mechanisms that occurred during current-carrying rolling in mixed atmospheres containing O₂ and H₂O vapor. The results obtained in a dry N₂/O₂ mixture, humid N₂, and humid N₂/O₂ mixture indicated that the oxidation mechanisms on current-carrying rolling surfaces involved thermal oxidation, tribo-oxidation, and anodic oxidation. XPS analysis confirmed that the primary oxidation product was CuO. Conductive atomic force microscopy (C-AFM) revealed that surface oxidation caused a significant reduction in conductive α-spots, leading to an increase in contact resistance. Contact resistance exhibited a quasi-linear relationship with the surface CuO content. Contact angle measurements and adhesion tests showed that the enhanced hydrophilicity of the oxidized surface and the resulting high adhesion contributed to an increase in the macroscopic friction coefficient. In humid N₂/O₂ with 50% relative humidity (RH), the friction coefficient rapidly exceeded 0.8 when the O₂ content surpassed 25%. Wear morphology analysis demonstrated that this abrupt increase in the friction coefficient induced fatigue wear on the surface. Overall, the present study elucidated the composite oxidation mechanisms during current-carrying rolling and clarified the pathways through which oxidation affected current-carrying tribological performance. These findings may contribute to improved failure analysis and the safe, reliable operation of electrical contact pairs.